Tm^(3+)/Dy^(3+)共掺铋酸盐玻璃的1.47μm宽带发光  

1.47μm Broadband Emission of Tm^(3+)/Dy^(3+) Co-Doped Bismuth Glass

作　　者：金文田 赵国营 徐玲芝 邱娟 侯京山 刘玉峰 房永征 廖梅松[2] 胡丽丽[2] Jin Wentian1, Zhao Guoying1, Xu Lingzhi1, Qiu Juan1, Hou Jingshan1, Liu Yufeng1, Fang Yongzneng1, Liao Meisong2, Hu Lili2(1. School of Materials Science and Engineering, Shanghai Institute of Technology, Shanghai 201418, China ;2. Key Laboratory of Materials for High Power Laser, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China)

机构地区：[1]上海应用技术大学材料科学与工程学院,上海201418 [2]中国科学院上海光学精密机械研究所强激光材料重点实验室,上海201800

出　　处：《中国激光》2018年第9期244-250,共7页Chinese Journal of Lasers

基　　金：国家自然科学基金(51472162;61605115);上海市扬帆计划(15YF1411800);上海应用技术大学特聘教授计划(TP2014061)

摘　　要：采用高温熔融法制备了Tm^(3+)/Dy^(3+)共掺杂铋酸盐玻璃样品。利用样品的差热分析曲线、拉曼光谱、红外透过光谱、吸收光谱、荧光光谱和荧光衰减曲线,对800nm激光二极管抽运下样品的1.47μm宽带发光特性进行了研究。研究结果表明,制备的铋酸盐玻璃具有良好的热稳定性、较低的声子能量和较高的红外透过率。当Dy^(3+)的摩尔分数为0.3%时,实现了对Tm^(3+)的1.47μm发光的敏化增强,其荧光谱线的半峰全宽为118nm。计算得到1.47μm发光的最大受激发射截面为4.37×10^(-21) cm^2,光纤放大品质因子为5.31×10^(-26) cm^3。The samples of the Tm^3＋/Dy^3＋ co-doped bismuth glasses are successfully prepared by the conventional high temperature melt-quenching method.By means of the differential scanning calorimetry curves,Raman spectra,absorption spectra,infrared transmittance spectra,fluorescence spectra and fluorescence decay curves of the samples,the 1.47μm broadband emission properties of the samples pumped by 800 nm laser diode（LD）are investigated.The results show that,the prepared bismuth glasses have a good thermal stability,a low phonon energy and a high infrared transmissivity.When the mole fraction of Dy^3＋ is 0.3%,the sensitivity enhancement of the 1.47μm emission of Tm^3＋ is achieved and the full-width at half-maximum of the fluorescence spectrum is 118 nm.The calculated maximum stimulated emission cross section of 1.47μm emission is 4.37×10^-21 cm^2 and the figure of merit for the fiber amplification is 5.31×10^-26 cm^3.

关 键 词：材料 铋酸盐玻璃 宽带近红外发光 铥镝共掺杂 光纤放大器 

分 类 号：TQ171[化学工程—玻璃工业]