Strength and Chloride Diffusion Behaviour of Three Generations of Repeated Recycled Fine Aggregate Concrete  

作　　者：ZHU Pinghua LIU Wenying NIU Zhigang WEI Da HU Kun 朱平华;LIU Wenying;牛志刚;WEI Da;胡坤(Department of Civil Engineering, Changzhou University;State Key Laboratory GeoMechanics and Deep Underground Engineering, China University of Mining & Technology,Xuzhou)

机构地区：[1]Department of Civil Engineering,Changzhou University,Changzhou 213164,China [2]State Key Laboratory GeoMechanics and Deep Underground Engineering,China University of Mining ＆ Technology,Xuzhou 221116,China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2018年第5期1113-1120,共8页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China(No.51278073);State Key Laboratoryfor GeoMechanics and Deep Underground Engineering,China University of Mining&Technology(No.SKLGDUEK1704)

摘　　要：The feasibility of using different generations of recycled fine aggregate（RFA） in structural concrete in a chloride environment was evaluated by studying the performance of the RFA and the corresponding concrete. The different generations of RFA were recycled by following the cycle of ‘concrete-waste concrete-fine aggregate-concrete＇. The properties of three generations of repeatedly recycled fine aggregate（RRFA） were systematically investigated, and we focused on the compressive strength and splitting tensile strength and chloride ion permeability of the related structural concretes with 25%, 75%, and 100% replacement of natural fine aggregates with RFA. The results indicated that the quality of RRFA presents a trend of slow deterioration, but the overall performance of all RRFA still fulfils the quality requirements of recycled fine aggregate for structural concrete. All RRFA concretes achieved the target compressive strength of 40 MPa after 28 days except for the second generation of the recycled aggregate concrete and the third generation of the recycled aggregate concrete with 100% replacement, and all the concrete mixes achieved the target compressive strength after 90 days. The insights obtained in this study demonstrate the feasibility of using at least three generations of RRFA for the production of normal structural concrete with a design service life of 100 years in a chloride environment.The feasibility of using different generations of recycled fine aggregate（RFA） in structural concrete in a chloride environment was evaluated by studying the performance of the RFA and the corresponding concrete. The different generations of RFA were recycled by following the cycle of ‘concrete-waste concrete-fine aggregate-concrete＇. The properties of three generations of repeatedly recycled fine aggregate（RRFA） were systematically investigated, and we focused on the compressive strength and splitting tensile strength and chloride ion permeability of the related structural concretes with 25%, 75%, and 100% replacement of natural fine aggregates with RFA. The results indicated that the quality of RRFA presents a trend of slow deterioration, but the overall performance of all RRFA still fulfils the quality requirements of recycled fine aggregate for structural concrete. All RRFA concretes achieved the target compressive strength of 40 MPa after 28 days except for the second generation of the recycled aggregate concrete and the third generation of the recycled aggregate concrete with 100% replacement, and all the concrete mixes achieved the target compressive strength after 90 days. The insights obtained in this study demonstrate the feasibility of using at least three generations of RRFA for the production of normal structural concrete with a design service life of 100 years in a chloride environment.

关 键 词：repeated recycled concrete repeatedly recycled fine aggregate compressive strength chloride ion diffusion 

分 类 号：TU528[建筑科学—建筑技术科学]