Al(OPhCH_3)(i-Bu)_2/Al Et_(1.5)Cl_(1.5)助催化剂一锅法合成含结晶结构的钼系高乙烯基聚丁二烯橡胶（英文）  

Mo-based high vinyl polybutadiene rubbers with crystalline structure prepared with Al(OPhCH_3)(i-Bu)_2/AlEt_(1.5)Cl_(1.5) cocatalysts by one-pot synthetic technology

作　　者：张彬彬 李培培 刘金慧[1] 华静[1] ZHANG Bin-bin, LI Pei-pei, LIU Jin-hui, HUA Jing(Key Laboratory of Rubber-Plastics of Ministry of Education, Qingdao University of Science ＆ Technology, Qingdao 266042, China)

机构地区：[1]青岛科技大学橡塑材料与工程教育部重点实验室,山东青岛266042

出　　处：《合成橡胶工业》2018年第6期476-476,共1页China Synthetic Rubber Industry

基　　金：Supported by Shandong Provincial Natural Science Foundation(ZR 2016 EMM 03)

摘　　要：以Al(OPhCH_3)(i-Bu)_2(简称Al_1)/AlEt_(1.5)Cl_(1.5)(简称Al_2)为助催化剂,采用一锅法,且先加入Al1/MoCl_5·磷酸三丁酯(TBP)催化丁二烯1,2-结构聚合为主,30 min后加入Al_2/MoCl_5·TBP催化体系继续引发聚合,结果表明,随着Al_2/Al_1(摩尔比)的增加,聚合物的1,2-结构含量降低,而反式-1,4-结构含量明显增加,在1,2-聚丁二烯相中产生反式-1,4-结晶微区。High vinyl polybutadiene rubbers （HVBR） with partially crystallized trans-1,4-polybutadiene rubbers were prepared by coordination polymerization of butadiene （Bd） catalyzed with two types of catalyst systems of MoCl5·tributyl phosphate （ TBP ） / Al （ OPhCH3 ） （i-Bu） 2 （ Mo/Al1 ）and MoCl5·TBP/A1Et1.5 Cl1.5 （ Mo/Al2 ） in one reactor, respectively.

关 键 词：乙烯基 聚丁二烯 钼系催化剂 烷基铝 结晶 

分 类 号：TQ333.2[化学工程—橡胶工业]