Plasmonic enhancement of upconversion emission in Ag@NaYF4:Er^3+/Yb^3+phosphor  

作　　者：S.K.Maurya S.R Tiwari A.Kumar K.Kumar 

机构地区：[1]Optical Materials and Bio-imaging Research Laboratory,Department of Applied Physics,Indian Institute of Technology(Indian School of Mines),Dhanhad-826004,India

出　　处：《Journal of Rare Earths》2018年第9期903-910,共8页稀土学报（英文版）

基　　金：Project supported by the Indian Institute of Technology(Indian School of Mines),Dhanbad,India;the Council of Scientific&Industrial Research(CSIR),New Delhi,India(03(1303)13/EMR)

摘　　要：In this article upconversion luminescence of silver nanoparticles（AgNPs） coated NaYF4：Er3＋/Yb3＋phosphor nano-particles was investigated.The prepared samples were characterized through various techniques.The surface plasmon band is observed for prepared AgNPs by analyzing UV-vis measurements and is used to enhance the upconversion emission.From the upconversion measurement the emission bands are observed at 522,546,and 656 nm corresponding to the 2 H11/2→ 4115/2,4 S3/2→4 I15/2and 4 F9/2→4 I15/2 levels,respectively.The upconversion emission intensity of the above bands is found to enhance for sample containing 1 mmol AgNPs.Decay time of 4 S3/2 and 4F9/2 levels is found to decrease on coating of AgNPs and hence intensity enhancement is assumed due to the surface plasmon resonance（SPR） effect.In this article upconversion luminescence of silver nanoparticles（AgNPs） coated NaYF4：Er3＋/Yb3＋phosphor nano-particles was investigated.The prepared samples were characterized through various techniques.The surface plasmon band is observed for prepared AgNPs by analyzing UV-vis measurements and is used to enhance the upconversion emission.From the upconversion measurement the emission bands are observed at 522,546,and 656 nm corresponding to the 2 H11/2→ 4115/2,4 S3/2→4 I15/2and 4 F9/2→4 I15/2 levels,respectively.The upconversion emission intensity of the above bands is found to enhance for sample containing 1 mmol AgNPs.Decay time of 4 S3/2 and 4F9/2 levels is found to decrease on coating of AgNPs and hence intensity enhancement is assumed due to the surface plasmon resonance（SPR） effect.

关 键 词：Upconversion phosphor Surface plasmon resonance Decay time analysis CIE diagram Rare earths 

分 类 号：TQ422[化学工程]