Luminescence of halophosphate solid-solution Ca5(PO4)3(F0.8Cl0.2)：Eu^2＋,Mn^2＋ for WLED  

作　　者：Jiashan Mao Hongwei Fang Yonghu Chen 

机构地区：[1]Department of Physics, University of Science and Technology of China, Hefei 230026, China [2]The Science and Technology Department of Fujian Province, Fuzhou 350003, China

出　　处：《Journal of Rare Earths》2018年第11期1157-1161,共5页稀土学报（英文版）

基　　金：Project supported by the National Natural Science Foundation of China(11574298,61635012);the National Key Research and Development Program of China(2016YFB0701001)

摘　　要：Solid-solution based luminescent materials have been widely explored due to their tunable optical properties in recent years. In this work, instead of more common cation-substitution approach, we investigated the luminescence properties of Eu^2＋ and Mn^2 ＋ co-doped halophosphate solid solution Ca5（PO4）3（F0.8Cl0.2） via anion substitution synthesized by high temperature solid state reaction method. The formation of the solid solution was confirmed by X-ray diffraction （XRD） characterization, which indicates that the introduction of certain proportion of CI will not make significant change on the CaB（PO4）3F lattice, We also studied the energy transfer from Eu^2＋ to Mn^2＋ in the host so as to obtain white light emission via adjusting the doping concentrations of Eu^2＋ and Mn^2＋, The white light emission was achieved through combination of Eu^2＋ blue emission and Mn^2＋ red-orange emission with appropriate proportions. The results suggest that Ca5（PO4）3（F0.8Cl0.2）：0.01Eu^2＋＋,0.18Mn^2＋ could be a potential WLED phosphor working under ultraviolet excitation,Solid-solution based luminescent materials have been widely explored due to their tunable optical properties in recent years. In this work, instead of more common cation-substitution approach, we investigated the luminescence properties of Eu^2＋ and Mn^2 ＋ co-doped halophosphate solid solution Ca5（PO4）3（F0.8Cl0.2） via anion substitution synthesized by high temperature solid state reaction method. The formation of the solid solution was confirmed by X-ray diffraction （XRD） characterization, which indicates that the introduction of certain proportion of CI will not make significant change on the CaB（PO4）3F lattice, We also studied the energy transfer from Eu^2＋ to Mn^2＋ in the host so as to obtain white light emission via adjusting the doping concentrations of Eu^2＋ and Mn^2＋, The white light emission was achieved through combination of Eu^2＋ blue emission and Mn^2＋ red-orange emission with appropriate proportions. The results suggest that Ca5（PO4）3（F0.8Cl0.2）：0.01Eu^2＋＋,0.18Mn^2＋ could be a potential WLED phosphor working under ultraviolet excitation,

关 键 词：WLED Rare earth Transition metal LUMINESCENCE Energy transfer 

分 类 号：TQ422[化学工程]