钢包内衬用MgO-CaO-C砖的开发与应用  

Development and application of MgO-CaO-C brick for ladle lining

作　　者：刘建辉[1] 陶绍平[1] 聂作禄[1] 王景彬 

机构地区：[1]首钢股份有限公司第二炼钢厂,北京100041 [2]辽宁大石桥金龙集团

出　　处：《耐火材料》2002年第4期221-223,共3页Refractories

摘　　要：采用抗水化处理后的镁钙砂为原料 ,研制了MgO -CaO -C砖 ,并对使用MgO -CaO -C砖过程中钢液中夹杂数量和氧含量的变化情况进行了分析。结果表明 :MgO -CaO -C砖在钢包包壁非渣线部位使用 ,能减少钢中氧含量和夹杂物数量 ,降低夹杂粒径 ,改变夹杂粒度分布 ,提高钢水质量。The MgO-CaO-C brick was prepared using the hydration-resistance treated magnesia-dolomite clinker as starting material.The inclusion amount and oxygen content in molten steel after using the developed MgO-CaO-C brick in ladle lining were analyzed and studied.It is found that constructing the MgO-CaO-C brick in nonslagline area in the sidewall of ladle can decrease the oxygen content and inclusion amount in molten steel and the inclusion size,change the particle size distribution of the inclusion and therefore improve the quality of the molten steel.

关 键 词：钢包 内衬 MgO-CaO-C砖 开发 应用 夹杂物 氧含量 

分 类 号：TQ175.79[化学工程—硅酸盐工业]