变形处理对Al-Ti-C中间合金的影响  

Influence of Deformation Process on the Al-Ti-C Master Alloy

作　　者：柳延辉[1] 刘相法[1] 王振卿[1] 刘相俊[1] 边秀房[1] 

机构地区：[1]山东大学材料液态结构及其遗传性教育部重点实验室,山东济南250061

出　　处：《热加工工艺》2002年第5期7-8,共2页Hot Working Technology

基　　金：国家自然科学基金资助项目 (50 1 71 0 37) ;教育部科学技术研究重点项目 (重点 0 1 1 0 5)

摘　　要：研究了变形处理对 Al- Ti- C中间合金细化效果的影响。研究表明 ,采用不同的变形手段对 Al- Ti- C中间合金变形以后 ,其细化效果明显下降 ,而且随变形量的增加 ,细化效果下降愈严重。作者分析了变形后 Al- Ti- C中间合金的微观组织 ,发现变形后 Ti Al3相呈断裂状态 ,而且在 Ti Al3相内部分布的 Ti C颗粒与其分离开来。作者认为这是造成 Al-Ti-It was investigated that the influences of deformation process on the grain refining effect of Al Ti C master alloy. The results showed that the grain refining effect of Al Ti C master alloy is decreased after deformation with different methods, and the more the deformation, the more the decreases of the grain refining of Al Ti C master alloy. It was analyzed that the TiAl 3 phases are broken after deformation, and that TiC particles inside TiAl 3 are separated from TiAl3 phases, which results in the reduction of grain refining effect.

关 键 词：变形处理 AL-TI-C中间合金 晶粒细化 铝合金 

分 类 号：TG146.21[一般工业技术—材料科学与工程]