大豆蛋白质塑料特性的研究  

Study on the Special Property of Soy Protein Plastics

作　　者：汪浩 黄华[2] 张隐西[2] 

机构地区：[1]山东齐鲁石化股份公司树脂所,山东淄博255400 [2]上海交通大学高分子材料研究所,上海200240

出　　处：《中国塑料》2002年第8期57-61,共5页China Plastics

摘　　要：考察了不同的湿度环境对大豆蛋白质塑料力学性能的影响 ,随着环境湿度提高 ,拉伸强度下降 ,断裂伸长率提高 ,差示扫描量热 (DSC)曲线的峰升高 ;拉伸强度随着测试温度的提高而下降并且在高温时如 14 0℃也能检测到拉伸强度 ;储能模量随温度升高而下降 ,随甘油含量的增加 ,力学损耗峰出现在更低的温度 ,随时间延长 ,模量逐渐升高 ,温度越高 ,模量升高越快。The atmespere moisture affects the mechanical and thermal properties of soy protein plastics. With the increasing humidity, the tensile strength decreases and the elongation at breakage and the peak area of the DSC curve increases. The tensile strength decreases with the increasing temperature, and it can be detected at high temperatures,such as 140℃. The storage modulus decreases with the temperature rising. The mechanical loss peak appears at lower temperature with the increasing amount of glycerin content. With the time passing by, the modulus increases gradually. The higher the temperature is, the faster the modulus increases.

关 键 词：大豆蛋白质塑料 高温拉伸性能 动态力学性能 扩展流变性能 

分 类 号：TQ321.4[化学工程—合成树脂塑料工业]