Microstructure and mechanical properties of high strength as-cast Ti-15-3 alloy  

作　　者：丁宏升 周建中 贾均 郭景杰 苏彦庆 傅恒志 

出　　处：《中国有色金属学会会刊：英文版》2002年第3期445-449,共5页Transactions of Nonferrous Metals Society of China

基　　金：Project (G2 0 0 0 0 672 0 2 -2 )supportedbytheNationalKeyFundamentalResearchandDevelopmentProgram

摘　　要：The effects of heat treatment and solidification cooling rate on the microstructure and mechanical properties of as cast Ti 15 3 alloy prepared by induction skull melting method were investigated. Results show that the microstructure of as cast Ti 15 3 alloy changes from the features of simplified and larger size of beta grains to finer grain size with increasing solidification cooling rate. After solution treatment and different ageing treatment, alpha phase precipitates in grains interior as well as in grain boundaries. Due to the modification of the precipitate phase, the tensile strength and elongation of the alloy are improved simultaneously. A good combination of the values of 1.406?GPa of σ b and 4.5% of δ was obtained, which will be satisfied the use of this kind of alloy in critical areas.The effects of heat treatment and solidification cooling rate on the microstructure and mechanical properties of as cast Ti 15 3 alloy prepared by induction skull melting method were investigated. Results show that the microstructure of as cast Ti 15 3 alloy changes from the features of simplified and larger size of beta grains to finer grain size with increasing solidification cooling rate. After solution treatment and different ageing treatment, alpha phase precipitates in grains interior as well as in grain boundaries. Due to the modification of the precipitate phase, the tensile strength and elongation of the alloy are improved simultaneously. A good combination of the values of 1.406?GPa of σ b and 4.5% of δ was obtained, which will be satisfied the use of this kind of alloy in critical areas.

关 键 词：高强度钛合金 铸造合金 机械性质 显微结构 

分 类 号：TG146.2[一般工业技术—材料科学与工程]