FGH96/GH4169高温合金惯性摩擦焊热变形组织及行为分析  

Forming process analysis of hot deformation microstructures during inertia friction welding of FGH96/GH4169 superalloy

作　　者：王彬[1] 黄继华[1] 张田仓[2] 季亚娟[2] 何胜春[2] Wang Bin;Huang Jihua;Zhang Tiancang;Ji Yajuan;He Shengchun(School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China;Beijing Aeronautical Manufacturing Technology Research Institute,Beijing 100024,China)

机构地区：[1]北京科技大学,北京100083 [2]北京航空制造工程研究所,北京100024

出　　处：《焊接》2017年第10期47-50,共4页Welding & Joining

摘　　要：建立了FGH96/GH4169惯性摩擦焊接头组织形成过程的有限元模型,分析了焊缝热变形组织和飞边的形成模式。结果表明,摩擦热的作用使近摩擦面处母材形成塑性层,塑性层在轴向顶锻力作用下发生塑性流动,形成拉长组织并在摩擦面高温、高压及高应变速率作用下发生动态再结晶,拉长组织边界消失,再结晶晶粒呈无序等轴状。摩擦面金属沿径向流动,在边缘处挤出,其摩擦面延伸侧受拉应力作用,最终形成卷曲飞边并实现自清理作用。he model of inertia friction welding of FGH96/GH4169was established and the forming process of the deformed grains in the joint was analyzed.The results show that the friction heat leads to the formation of the plastic layer near the interface,the plastic layer flow under the stress and results in the formation of the deformed grains.Eventually the boundary of the deformed grains are broken,and the weld zone consists of refined and equiaxed grains.The plastic metals on the interface flow on radial direction and are squeezed to form the flash on the edge.The flash can take the inclusions out friction interface shows self clean effect.

关 键 词：高温合金 惯性摩擦焊 热变形组织 

分 类 号：TG453[金属学及工艺—焊接]