Roasting and leaching behaviors of vanadium and chromium in calcification roasting–acid leaching of high-chromium vanadium slag  

作　　者：Jing Wen Tao Jiang Mi Zhou Hui-yang Gao Jia-yi Liu Xiang-xin Xue 

机构地区：[1]School of Metallurgy,Northeastern University [2]Liaoning Key Laboratory for Recycling Science of Metallurgical Resources

出　　处：《International Journal of Minerals,Metallurgy and Materials》2018年第5期515-526,共12页矿物冶金与材料学报（英文版）

基　　金：financially supported by the National Natural Science Foundation of China (Nos.51604065 and 51574082);the National Basic Research Program of China (No.2013CB632603);the Fundamental Funds for the Central Universities (Nos.150203003 and 150202001)

摘　　要：Calcification roasting–acid leaching of high-chromium vanadium slag(HCVS)was conducted to elucidate the roasting and leaching behaviors of vanadium and chromium.The effects of the purity of Ca O,molar ratio between Ca O and V_2O_5(n(Ca O)/n(V_2O_5)),roasting temperature,holding time,and the heating rate used in the oxidation–calcification processes were investigated.The roasting process and mechanism were analyzed by X-ray diffraction(XRD),scanning electron microscopy(SEM),and thermogravimetry–differential scanning calorimetry(TG–DSC).The results show that most of vanadium reacted with Ca O to generate calcium vanadates and transferred into the leaching liquid,whereas almost all of the chromium remained in the leaching residue in the form of(Fe_(0.6)Cr_(0.4))_2O_3.Variation trends of the vanadium and chromium leaching ratios were always opposite because of the competitive reactions of oxidation and calcification between vanadium and chromium with Ca O.Moreover,Ca O was more likely to combine with vanadium,as further confirmed by thermodynamic analysis.When the HCVS with Ca O added in an n(Ca O)/n(V_2O_5)ratio of 0.5 was roasted in an air atmosphere at a heating rate of 10°C/min from room temperature to 950°C and maintained at this temperature for 60 min,the leaching ratios of vanadium and chromium reached91.14%and 0.49%,respectively;thus,efficient extraction of vanadium from HCVS was achieved and the leaching residue could be used as a new raw material for the extraction of chromium.Furthermore,the oxidation and calcification reactions of the spinel phases occurred at 592and 630°C for n(Ca O)/n(V_2O_5)ratios of 0.5 and 5,respectively.Calcification roasting–acid leaching of high-chromium vanadium slag(HCVS)was conducted to elucidate the roasting and leaching behaviors of vanadium and chromium.The effects of the purity of Ca O,molar ratio between Ca O and V_2O_5(n(Ca O)/n(V_2O_5)),roasting temperature,holding time,and the heating rate used in the oxidation–calcification processes were investigated.The roasting process and mechanism were analyzed by X-ray diffraction(XRD),scanning electron microscopy(SEM),and thermogravimetry–differential scanning calorimetry(TG–DSC).The results show that most of vanadium reacted with Ca O to generate calcium vanadates and transferred into the leaching liquid,whereas almost all of the chromium remained in the leaching residue in the form of(Fe_(0.6)Cr_(0.4))_2O_3.Variation trends of the vanadium and chromium leaching ratios were always opposite because of the competitive reactions of oxidation and calcification between vanadium and chromium with Ca O.Moreover,Ca O was more likely to combine with vanadium,as further confirmed by thermodynamic analysis.When the HCVS with Ca O added in an n(Ca O)/n(V_2O_5)ratio of 0.5 was roasted in an air atmosphere at a heating rate of 10°C/min from room temperature to 950°C and maintained at this temperature for 60 min,the leaching ratios of vanadium and chromium reached91.14%and 0.49%,respectively;thus,efficient extraction of vanadium from HCVS was achieved and the leaching residue could be used as a new raw material for the extraction of chromium.Furthermore,the oxidation and calcification reactions of the spinel phases occurred at 592and 630°C for n(Ca O)/n(V_2O_5)ratios of 0.5 and 5,respectively.

关 键 词：high-chromium VANADIUM slag CALCIFICATION ROASTING ROASTING BEHAVIORS leaching BEHAVIORS VANADIUM extraction 

分 类 号：TF791[冶金工程—钢铁冶金] TF841.3