作 者:赵青[1] ZHAO Qing(Taihu Universtiy of Wuxi,Wuxi,Jiangsu 214000,China)
机构地区:[1]无锡太湖学院,江苏无锡214000
出 处:《毛纺科技》2018年第4期23-26,共4页Wool Textile Journal
摘 要:探讨了氧化石墨烯对粘胶织物整理前后织物性能的变化。研究表明:粘胶织物经氧化石墨烯整理后,织物表面比电阻值降低了8个数量级,极大地改善了粘胶织物的抗静电性能;导热性能与抗紫外线性能分别提高了38.9%与61倍多,同时整理后粘胶织物的断裂强力变化幅度仅为4.4%,因此氧化石墨烯整理很好的改善了粘胶织物的功能性,是一种较为理想的功能性整理工艺。综合考虑整理后粘胶织物的性能与整理工艺成本,认为当粘胶织物表面氧化石墨烯覆盖量达到250 mg/m^2为最佳覆盖量。Properties influences of viscose fabric finished by oxidized graphene were studied by testing viscose fabrics properties of electric conduction,heat conduction,uvioresistant and mechanics before and after oxidized graphene finish.Research showed that properties of fabric superficies was decreased 8 order of magnitudes which properties of electric conduction was improved greatly;properties of fabric heat conduction and uvioresistant was increased 38.9%and 61 times and breaking strength was decreased 4.4%.All these modification data of properties of viscose fabric finished by oxidized graphene were demonstrated that viscose fabric finished by oxidized graphene was a perfect way of functional modification finish.Considering the properties of the viscose fabric after finishing and processing cost,it was believed that the best oxidized graphene overlay quantity was 250 mg/m2.
关 键 词:氧化石墨烯 粘胶织物 导电性能 导热性能 抗紫外线性能 力学性能
分 类 号:TS193.22[轻工技术与工程—纺织化学与染整工程]
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在链接到云南高校图书馆文献保障联盟下载...
云南高校图书馆联盟文献共享服务平台 版权所有©
您的IP:216.73.216.38