皮秒激光旋切加工微孔试验研究  

Experimental study about micro hole processing by picosecond laser

作　　者：孙树峰 廖惠鹏[2] 吴旭浩 章斌 SUN Shufeng;LIAO Huipeng;WU Xuhao;ZHANG Bin(School of Mechanical Engineering,Qingdao University of Technology,Qingdao 266520,China;School of Mechanical and Electrical Engineering,Wenzhou University,Wenzhou 325035,China;High laser Opto-Electronic Technology Co.Ltd.,Wenzhou 325035,China)

机构地区：[1]青岛理工大学机械工程学院,青岛266520 [2]温州大学机电工程学院,温州325035 [3]浙江久恒光电科技有限公司,温州325035

出　　处：《激光技术》2018年第2期234-238,共5页Laser Technology

基　　金：国家自然科学基金资助项目(51775289);山东省科技厅重大关键技术资助项目(2016ZDJS02A15);山东省泰山学者工程专项经费资助项目(ts201511038);温州市科技局公益性科技计划资助项目(G20170014);青岛市创新领军人才计划资助项目

摘　　要：为了解决毫/纳秒激光加工微孔质量低的问题,利用脉冲宽度为200ps的脉冲激光,采用高速旋切法对厚度为0.2mm的SUS 304不锈钢薄板进行直径为200μm的微孔加工试验,用激光共聚焦显微镜观察孔的外观形貌,研究旋切速率、激光功率和离焦量等因素对孔径、锥度和热影响区等加工质量的影响。结果表明,旋切速率对微孔内壁质量有直接的影响;通过提高转速来降低激光脉冲重叠率可以减小微孔内壁的热影响区;适当增加激光功率,能够改善旋切加工微孔切口处的加工质量;采用正离焦加工能够一定程度减小孔的锥度。优化工艺参量能够加工出热影响区小、边缘质量好的小锥度微孔。In order to solve the problem of low quality of micro hole processed by micro/nanosecond laser,using pulse laser with pulse width of 200ps and high speed rotary cutting method,a micropore process test with a diameter of 200μm was conducted on SUS 304 stainless steel sheet with thickness of 0.2mm.The morphologies of the micro holes were observed by laser scanning confocal microscope.The effects of cutting speed,laser power and defocusing distance on machining quality of aperture,taper and heat affected zone were investigated.The results show that,the cutting speed has the direct influence on the quality of micro porous wall.By increasing the rotating speed,the overlap rate of laser pulse and the heat affected zone of the inner wall of micro hole can be reduced.At the same time,the machining quality of micro incision by rotary cutting method can be improved by increasing laser power.The taper of micro hole can be reduced to a certain extent by adopting positive defocusing machining.The study shows that,the optimized technological parameters can be used to process small taper pores with small heat affected zone and good edge quality.

关 键 词：激光技术 微孔 高速旋切法 皮秒激光 脉冲重叠率 锥度 

分 类 号：TG665[金属学及工艺—金属切削加工及机床]