Mg元素对碳纳米管/钛铝合金复合材料组织与性能的影响  

Effect of Mg on Microstructure and properties of carbon nanotubes/titanium aluminum alloy composites

作　　者：刘慧[1] 郭俊 LIU Hui;GUO Jun(School of materials science and engineering,Anhui University of Technology,Ma'anshan 243002,China)

机构地区：[1]安徽工业大学材料科学与工程学院,安徽马鞍山243002

出　　处：《世界有色金属》2018年第10期198-199,共2页World Nonferrous Metals

基　　金：安徽省高校自然科学研究资助项目(2016/KJ2016A807)

摘　　要：本文利用充氢球磨与热压烧结技术制备碳纳米管/钛铝合金复合材料,在此期间加入少量Mg元素,分析其对材料组织与性能的影响。分析结果表明:当Mg含量为1.0at.%时,材料的组织更加均匀和细化,在添加2.0at.%Mg元素的复合材料中出现了层片状组织。添加1.0at.%Mg元素的复合材料的显微硬度提高了24%,达到了814.7HV,但随Mg含量的增加硬度显著降低;断口处观察到的碳纳米管形貌呈现撕裂状。We analyzed the influence of Mg on the microstructure and properties of the prepared composites by ball milling and hot pressing sintering.The results showed that the microstructure was uniform and refined with 1.0at.%Mg.Lamellar microstructure appeared in the composites with the addition of 2.0at.%Mg element.The micro hardness of the composites with 1.0at.%Mg reached 814.7HV,increasing 24%than that without Mg,but decreased significantly with the addition of Mg.The CNTs in the fracture surface is tear.

关 键 词：Mg元素 钛铝合金 复合材料 组织与性能 