Preparation of Mesoporous ZSM-5 Zeolite under Double Ester Base Long Carbon Chains Organosilane Quaternary Ammonium Salt Template Agent  

作　　者：QIAO Wenjua LIU Dongliang 乔文娟;刘栋良

机构地区：[1]College of Chemistry,Chemical Engineering & Biotechnology,Donghua University

出　　处：《Journal of Donghua University(English Edition)》2018年第5期380-383,共4页东华大学学报（英文版）

基　　金：National Natural Science Foundation of China(No.21676053)

摘　　要：The pore sizes of traditional zeolites are in the range of0. 3-1. 5 nm,which strongly hinder the diffusion of large reactant and product molecules within the zeolite pores. To compensate for it,we tried to create mesopores in traditional microporous zeolites and retain all advantages of microporous zeolites. Mesoporous Zeolite Socony Mobile-Five( ZSM-5) zeolite was synthesized by a new double ester base long carbon chains organosilane quaternary ammonium salt as the soft template agent in hydrothermal method.The structure of the acquired zeolite crystals was confirmed by fieldemission scanning electron microscopy( FE-SEM), transmission electron microscopy( TEM), nitrogen adsorption-desorption measurements and X-ray diffraction( XRD),which indicated that their structure had the same characteristics as traditional ZSM-5 zeolites. Compared with traditional ZSM-5 zeolite,there were 4 nm and 15 nm mesopores in the crystal. The prepared hierarchical porous ZSM-5 zeolite was expected to be effective catalytic materials for chemical reactions involving large molecules.The pore sizes of traditional zeolites are in the range of0. 3-1. 5 nm,which strongly hinder the diffusion of large reactant and product molecules within the zeolite pores. To compensate for it,we tried to create mesopores in traditional microporous zeolites and retain all advantages of microporous zeolites. Mesoporous Zeolite Socony Mobile-Five( ZSM-5) zeolite was synthesized by a new double ester base long carbon chains organosilane quaternary ammonium salt as the soft template agent in hydrothermal method.The structure of the acquired zeolite crystals was confirmed by fieldemission scanning electron microscopy( FE-SEM), transmission electron microscopy( TEM), nitrogen adsorption-desorption measurements and X-ray diffraction( XRD),which indicated that their structure had the same characteristics as traditional ZSM-5 zeolites. Compared with traditional ZSM-5 zeolite,there were 4 nm and 15 nm mesopores in the crystal. The prepared hierarchical porous ZSM-5 zeolite was expected to be effective catalytic materials for chemical reactions involving large molecules.

关 键 词：MESOPOROUS ZEOLITE Socony Mobile-Five(ZSM-5)zeolite DOUBLE long carbon chains ORGANOSILANE QUATERNARY AMMONIUM salt 

分 类 号：O69[理学—化学]