Optimization of wear parameters of binary Al-25Zn and Al-3Cu alloys using design of experiments  

作　　者：Sreejith J S.Ilangovan 

机构地区：[1]Department of Mechanical Engineering, Amrita School of Engineering

出　　处：《International Journal of Minerals,Metallurgy and Materials》2018年第12期1465-1472,共8页矿物冶金与材料学报（英文版）

摘　　要：Zinc-aluminum alloys have been used as bearing materials in the past. In recent years, binary Al-Zn alloys and Al-Zn-Cu alloys are being used as an alternative to the Zn-Al alloys for bearing applications. In this study, both binary Al-25 Zn and Al-3 Cu were prepared using stir casting process. Homogenization of the as-cast alloys was performed at 350oC for 8 h and then, the alloys were furnace-cooled to 50oC. The homogenization led to the removal of the dendritic structure of the as-cast alloys. After homogenization, wear parameters optimization was carried out using Taguchi technique. For this purpose, L9 orthogonal array was selected, and the control parameters selected are load, velocity, and sliding distance. The optimum parametric condition was obtained using signal-to-noise(S/N) ratio analysis, and specific wear rate(SWR) is the selected response. The "smaller-the-better" is the goal of the experiment for S/N ratio analysis. After the optimization, confirmation tests were carried out using analysis of variance(ANOVA) from the developed regression equation. Finally, wear mechanism studies were conducted using scanning electron microscopy(SEM) and energy-dispersive X-ray spectroscopy(EDX) images.Zinc-aluminum alloys have been used as bearing materials in the past. In recent years, binary Al-Zn alloys and Al-Zn-Cu alloys are being used as an alternative to the Zn-Al alloys for bearing applications. In this study, both binary Al-25 Zn and Al-3 Cu were prepared using stir casting process. Homogenization of the as-cast alloys was performed at 350oC for 8 h and then, the alloys were furnace-cooled to 50oC. The homogenization led to the removal of the dendritic structure of the as-cast alloys. After homogenization, wear parameters optimization was carried out using Taguchi technique. For this purpose, L9 orthogonal array was selected, and the control parameters selected are load, velocity, and sliding distance. The optimum parametric condition was obtained using signal-to-noise(S/N) ratio analysis, and specific wear rate(SWR) is the selected response. The "smaller-the-better" is the goal of the experiment for S/N ratio analysis. After the optimization, confirmation tests were carried out using analysis of variance(ANOVA) from the developed regression equation. Finally, wear mechanism studies were conducted using scanning electron microscopy(SEM) and energy-dispersive X-ray spectroscopy(EDX) images.

关 键 词：specific WEAR rate micro-hardness Taguchi technique SIGNAL-TO-NOISE ratio analysis of variance aluminum-zinc ALLOY aluminum-copper ALLOY 

分 类 号：TF[冶金工程]