Silicalite-1修饰的HY型分子筛及其对纤维素水解的催化性能  

Catalytic performance of silicalite-1 modified HY zeolite in the hydrolysis of cellulose

作　　者：于杰 王景芸[2] 王震[2] 周明东 王海彦[1,2] YU Jie;WANG Jing-yun;WANG Zhen;ZHOU Ming-dong;WANG Hai-yan(College of Chemical Engineering,China University of Petroleum,Qingdao 266580,China;School of Chemistry and Materials Science,Liaoning Shihua University,Fushun 113001,China;Shenyang Paraffin Chemical Co Ltd,Shenyang 110141,China)

机构地区：[1]中国石油大学(华东)化学工程学院,山东青岛266580 [2]辽宁石油化工大学化学与材料科学学院,辽宁抚顺113001 [3]沈阳石蜡化工有限公司,辽宁沈阳110141

出　　处：《燃料化学学报》2018年第12期1447-1453,共7页Journal of Fuel Chemistry and Technology

基　　金：国家自然科学基金(21101085);辽宁省自然科学基金(2015020196;20170540590);抚顺科学计划(FSKJHT 201423);辽宁高校优秀人才培养计划(LJQ2012031);辽宁石油化工大学博士科研启动基金项目(2016XJJ-063)资助~~

摘　　要：采用silicalite-1对HY型分子筛进行修饰,得到具有核壳结构的复合分子筛HY/silicalite-1。通过X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、N2的吸附-脱附及吡啶吸附红外(Py-FTIR)等手段对不同晶化时间合成的HY/silicalite-1复合分子筛进行了表征,研究了复合分子筛对纤维素水解的催化性能。结果表明,晶化时间直接影响复合分子筛的晶体生长规律和两组分的相对含量,最佳晶化时间为16-24 h,所得到的复合分子筛外貌呈核壳结构,silicalite-1附晶生长在HY型分子筛的表面;随着晶化时间的延长,复合分子筛的表面由胶浊状变为光滑,最终变为鳞片状;其B酸量先减少后增加,而L酸量则先增加后减少。其中,晶化时间为24 h的HY/silicalite-1复合分子筛B酸量最大,L酸量最小,对纤维素水解反应具有良好的催化性能,葡萄糖收率由HY型分子筛催化获得的28.0%大幅提高至45.8%。A core-shell composite zeolite(HY/silicalite-1)was prepared by modifying HY zeolite with silicalite-1 and characterized by X-ray diffraction(XRD),Scanning electron microscope(SEM),Transmission electron microscope(TEM),N 2 sorption and IR spectra of pyridine adsorption(Py-FTIR);the catalytic performance of HY/silicalite-1 composite zeolite in the hydrolysis of cellulose was then investigated in comparison with that of HY.The results show that the crystallization time has a significant influence on the crystal growth of the HY/silicalite-1 composite zeolite and the relative content of two components.With the optimum crystallization time of 16-24 h,a core-shell structure for the HY/silicalite-1 composite zeolite is achieved,where the silicalite-1 crystal grows over the surface of HY zeolite;with the prolongation of the crystallization time,the morphology of the composite zeolite changes from rough turbid to smooth and eventually to scale-like surface.The amount of Br nsted acid sites decreases first and then increases with the increase of the crystallization time,whereas the amount of Lewis acid sites changes in the opposite direction.In particular,the HY/silicalite-1 composite zeolite obtained with a crystallization time of 24 h exhibits excellent catalytic performance in the hydrolysis of cellulose to glucose;over it,the yield of glucose reaches 45.8%at 130℃,much higher than the value of 28.0%over the HY zeolite.

关 键 词：复合分子筛 SILICALITE-1 HY 纤维素 水解 晶化时间 