无溶剂蓖麻油聚酯多元醇的合成及应用研究  

Synthesis and Application of Solvent-Free Castor Oil Polyester Polyol

作　　者：王长坤 梁亮[1] 蒲永祥 汪松青 Wang Changkun;Liang Liang;Pu Yongxiang;Wang Songqing(School of Chemical Engineering and Light Industry,Guangdong University of Technology,Guangzhou 510006,China;Carpoly Chemical Group Co.,Ltd.,Jiangmen,Guangdong 529085,China;Guangdong Deliya New Material Co.,Ltd.,Shaoguan,guangdong 512627,China)

机构地区：[1]广东工业大学轻工化工学院,广州510006 [2]嘉宝莉化工集团股份有限公司,广东江门529085 [3]广东德丽雅新材料有限公司,广东韶关512627

出　　处：《涂料工业》2019年第3期14-19,共6页Paint & Coatings Industry

摘　　要：以菴麻油、甘油、己二酸和乙二醇为原料,酯化缩聚合成低黏度的菖麻油聚酯多元醇,并将该萌麻油聚酯多元醇与HDI聚异氧酸酯制备无溶剂涂料。研究了醇酸比[n(一0H):n(—COOH)]对菴麻油聚酯多元醇及其涂层性能的影响。结果表明:在醇酸比为1.32时,艷麻油聚酯多元醇所制涂层的耐水性、耐冲击性、耐擦伤性、柔韧性等综合性能良好。A castor oil-modified polyester polyol with low viscosity was synthesized via polycondensation by using castor oil, glycerin and adipic acid as raw materials. Then solvent- free coatings were prepared from the modified polyester polyol and HDI polyisocyanate. The effect of the mol ratio of alkyd on the properties of castor oil-modified polyester polyol and its solvent-free coating was investigated. The result showed that when the mol ratio of alkyd was 1.32, the solvent-free coating had good comprehensive properties such as water resistance, impact resistance, scratch resistance and flexibility.

关 键 词：蓖麻油 聚酯多元醇 无溶剂涂料 

分 类 号：TQ637.84[化学工程—精细化工]