高强双相钢DP1180平整轧制研究与实践  

Research and Practice of Skin Pass Rolling of High Strength Steel DP1180

作　　者：李靖[1] 关军[1] 任志超[1] 王飞[1] 王少飞[1] 巫雪松 LI Jing;GUAN Jun;REN Zhichao;WANG Fei;WANG Shaofei;WU Xuesong(Shougang Jingtang United Iron & Steel Co.,Ltd.)

机构地区：[1]首钢京唐钢铁联合有限责任公司

出　　处：《首钢科技》2019年第1期41-43,共3页Shougang Science and Technology

摘　　要：强双相钢DP1180兼有高强度和一定成形性,是汽车结构件的重要材料。由于髙强双相钢DP1180抗拉强度在1180MPa以上,平整难度极大,在轧制过程中易出现轧制力大、边浪和延伸率不合格等问题。通过对该钢种在平整轧制过程中出现的问题进行剖析,提出了相应的针对性措施.解决了高强双相钢DP1180在轧制过程中出现的问题,获得了良好的实践效果。High strength steel DP1180,which had both high strength and some fonnability,was an important material for automobile structural parts.Because the tensile strength of high strength steel DP1180 was above 1 180 MPa,the skin pass rolling process was very difficult.In the rolling process,problems such as heavy rolling force,edge wave and unqualified elongation were prone to occur.By analyzing the problems occurred in the skin pass rolling process,the corresponding measures were put forward to solve the problems,and good practical results were obtained.

关 键 词：高强钢 DP1180 平整 

分 类 号：TG335.56[金属学及工艺—金属压力加工]