FeCrAl铁素体不锈钢在压水堆水化学偏离工况下的应力腐蚀行为  

Stress Corrosion Behavior of FeCrAl Ferrite Stainless Steel under PWR Water Deviation Condition

作　　者：肖婷 肖军[1] 陈勇[1] 周军[1] 王辉[1] XIAO Ting;XIAO Jun;CHEN Yong;ZHOU Jun;WANG Hui(Science and Technology on Reactor Fuel and Materials Laboratory,Nuclear Power Institute of China, Chengdu 610213, China)

机构地区：[1]中国核动力研究设计院反应堆燃料及材料重点实验室,四川成都610213

出　　处：《原子能科学技术》2019年第3期414-419,共6页Atomic Energy Science and Technology

摘　　要：采用慢应变速率拉伸(SSRT)试验方法,研究了FeCrAl铁素体不锈钢在偏离压水堆正常工况下的应力腐蚀行为。结果表明,在含有微量Cu^(2+)与Cl^-的高温水介质中,应变速率为2×10^(-7) s^(-1)时,FeCrAl铁素体不锈钢将发生显著的应力腐蚀开裂;其在含Cu^(2+)和Cl^-的高温水介质中的应力腐蚀开裂主要由点蚀导致。Stress corrosion behavior of FeCrAl ferrite stainless steel under PWR water deviation condition was investigated by slow strain rate tensile (SSRT) tests. The results show that FeCrAl ferrite stainless steel is subject to stress corrosion cracking (SCC) at strain rate of 2×10 ^-7 s ^-1 , with the co-exist of Cu^2+ and Cl^- in water. SCC of FeCrAl ferrite stainless steel in high temperature water containing Cu^2+ and Cl^- is considered to result from pitting corrosion.

关 键 词：应力腐蚀开裂 FeCrAl铁素体不锈钢 慢应变速率拉伸 

分 类 号：TL33[核科学技术—核技术及应用]