离子液体增塑聚酰胺6纤维的制备与性能表征  

Preparation and property characterization of ionic liquid plasticized polyamide 6 fibers

作　　者：吉鹏[1] 唐自远 陈仕艳[2] 王朝生[2] Ji Peng;Tang Ziyuan;Chen Shiyan;Wang Chaosheng(Co-Innovation Center for Textile Industry,Donghua University,Shanghai 201620;State Key Laboratory for Modification of Chemical Fibers and Polymer Materials,College of Materials Science and Engineering,Donghua University,Shanghai,201620)

机构地区：[1]东华大学纺织产业关键技术协同创新中心,上海201620 [2]东华大学材料科学与工程学院纤维材料改性国家重点实验室,上海201620

出　　处：《合成纤维工业》2019年第2期11-15,共5页China Synthetic Fiber Industry

基　　金：国家重点研发计划项目(2016YFB0302703);中央高校基本科研业务费专项资金资助(19D128201)

摘　　要：在聚酰胺6(PA 6)中添加离子液体对其进行增塑改性制得离子液体增塑PA 6切片,再经熔融纺丝、拉伸、定型,制备离子液体增塑PA 6纤维,然后对纤维试样进行水洗;探讨了离子液体含量对增塑PA 6纤维的热性能、动态力学性能、取向及力学性能的影响以及水洗之后纤维力学性能的变化。结果表明:随着离子液体添加量的增加,增塑PA 6纤维的熔融温度与结晶温度逐渐下降,纤维分子链的活动性增加,玻璃化转变温度逐渐下降;离子液体并未提高增塑PA 6纤维的取向度;随着离子液体含量的增加,增塑PA 6纤维的断裂强度先增加后降低,断裂伸长率呈下降趋势;在离子液体质量分数为1.5%、拉伸倍数为3.6时,增塑PA 6纤维的断裂强度最高,达3.89 cN/dtex,纤维水洗后断裂强度大幅度提高,达6.36 cN/dtex。Polyamide 6(PA 6)was exposed to plasticization modification by adding ionic liquid to prepare an ionic liquid plasticized PA 6 chip which was produced into ionic liquid plasticized PA 6 fiber by melt spinning,drawing and setting processes.The fiber samples were subjected to water washing.The effects of ionic liquid content on the thermal property,dynamic mechanical properties,orientation and mechanical properties of ionic liquid plasticized PA 6 fiber were discussed,as was the change of mechanical properties of the fiber after water washing.The results showed that the melting temperature and crystallization temperature of the fiber gradually decreased,the activity of the molecular chains increased,and the glass transition temperature gradually decreased with the addition of ionic liquid;the ionic liquid did not enhance the orientation of plasticized PA 6 fiber;the breaking strength of the plasticized PA 6 fiber first increased and then decreased and the elongation at break appeared a downward tendency when the ionic liquid content was increased;and the breaking strength of the plasticized PA 6 fiber was maximized as 3.89 cN/dtex at the mass fraction of ionic liquid of 1.5%and the draw ratio of 3.6 and considerably increased to 6.36 cN/dtex after water washing.

关 键 词：聚酰胺6纤维 离子液体 增塑改性 水洗 力学性能 热性能 

分 类 号：TQ342.11[化学工程—化纤工业]