改性双马来酰亚胺/苯并嗪共混树脂性能的研究  

Study on the property of modified bismaleimide and benzoxazine blend

作　　者：段宪法 李玲[1] 赵晓芳 于永建 刘翔宇 Duan Xianfa;Li Ling;Zhao Xiaofang;Yu Yongjian;Liu Xiangyu(School of Materials Science and Engineering,North University of China,Taiyuan 030051)

机构地区：[1]中北大学材料科学与工程学院,太原030051

出　　处：《化工新型材料》2019年第4期96-99,共4页New Chemical Materials

摘　　要：双酚A型苯并嗪(BOZ)与改性双马来酰亚胺(m-BMI)以不同比例共混制备了m-BMI/BOZ浇铸体及其玻璃纤维复合材料,研究了m-BMI/BOZ树脂体系的固化特性和力学性能。结果表明,m-BMI/BOZ树脂体系的凝胶时间随m-BMI含量的增加而缩短。体系固化过程中出现两个放热峰,其特征固化峰值温度随m-BMI含量的增加而降低。浇铸体和层压板的弯曲强度、弯曲模量和冲击强度随m-BMI含量的提高显著增强。The bisphenol A based benzoxazine(BOZ)and the modified bismaleimide(m-BMI)were blended in various proportions,and the m-BMI/BOZ casting body and its glass fiber composites was prepared,and the curing characteristics and mechanical properties of m-BMI/BOZ resin systems were studied.The results showed that the gel time of m-BMI/BOZ was shortened with the increase of m-BMI content.The curing reaction of m-BMI/BOZ had two exothermic peak,and the peak temperature of typical curing exotherm was decreased with increasing m-BMI content.The flexural strength,flexural modulus and impact strength of casting body and laminate increased significantly with increasing m-BMI content.

关 键 词：苯并噁嗪 双马来酰亚胺 复合材料 固化特性 力学性能 

分 类 号：TB33[一般工业技术—材料科学与工程]