SiO2的质量浓度对Zn-Ni-P/SiO2复合镀层耐蚀性的影响  

Influence of Mass Concentration of SiO2 on Corrosion Resistance of Zn-Ni-P/SiO2 Composite Coatings

作　　者：刘军松 刘定富[1] 方舒[1] LIU Junsong;LIU Dingfu;FANG Shu(School of Chemistry and Chemical Engineering,Guizhou University,Guiyang 550025,China)

机构地区：[1]贵州大学化学与化工学院

出　　处：《电镀与环保》2019年第3期10-12,共3页Electroplating & Pollution Control

摘　　要：向Zn-Ni-P合金镀液中添加纳米SiO2微粒,获得了Zn-Ni-P/SiO2复合镀层。通过电化学测试及盐水浸泡试验,研究了SiO2的质量浓度对Zn-Ni-P/SiO2复合镀层耐蚀性的影响。结果表明:随着SiO2的质量浓度的增加,镀层的耐蚀性先增强后减弱;当SiO2的质量浓度为8 g/L时,镀层的耐蚀性最好。Zn-Ni-P/SiO2 composite coatings were prepared from Zn-Ni-P alloy plating bath containing nano-SiO2 particles.The mass concentration of SiO2 on the corrosion resistance ofZn-Ni-P/SiO2 composite coatings was studied by electrochemical test and brine immersion test.The results showed that the corrosion resistance of the coatings improved first and then declined with the increasing of the mass concentration of SiO2.When the mass concentration of SiO2 was8 g/L,the coating has the best corrosion resistance.

关 键 词：Zn-Ni-P/SiO2复合镀层 纳米SiO2微粒 耐蚀性 

分 类 号：TQ153[化学工程—电化学工业]