高门尼、易加工密封条用乙丙共聚物的合成  

Synthesis of ethylene-propylene rubber for sealing strip

作　　者：王笑海[1] 王雨晴 冯克新 刘乐然 张春英[1] 杨博[1] 刘振国[1] 宫立波[1] WANG Xiaohai;WANG Yuqing;FENG Kexin;LIU Leran;ZHANG Chunying;YANG Bo;LIU Zhenguo;GONG Libo(Research Institute of Jilin Petrochemical Company,PetroChina,Jilin 132021,China;Jilin Mengxi Engineering Management Company,Ltd.,Jilin 132021;Organic Synthesis Plant of Jilin Petrochemical Company,PetroChina,Jilin 132021,China;Calcium Carbide Plant of Jilin Petrochemical Company,PetroChina,Jilin 132021,China)

机构地区：[1]中国石油吉林石化公司研究院,吉林吉林132021 [2]吉林梦溪工程管理有限公司,吉林吉林132021 [3]中国石油吉林石化公司有机合成厂,吉林吉林132021 [4]中国石油吉林石化公司电石厂,吉林吉林132021

出　　处：《弹性体》2019年第3期56-59,共4页China Elastomerics

基　　金：中国石油吉林石化公司重点科研项目(F765018H5)

摘　　要：采用二氯乙氧基氧钒(Vx)为主催化剂,以倍半氯化乙基铝(AQ)为助催化剂,乙烯、丙烯为聚合单体,乙叉降冰片烯(ENB)为第三单体,己烷为聚合溶剂,均相聚合合成高、低门尼黏度乙烯丙烯三元共聚物,采用并联掺混法分别合成高分子质量部分乙丙共聚物和低分子质量部分乙丙共聚物,然后二者按比例进行掺混。高分子质量部分的乙丙共聚物为高乙烯含量、低ENB含量的乙丙共聚物;低分子质量部分的乙丙共聚物为低乙烯含量、高ENB含量的乙丙共聚物,高门尼黏度部分的乙丙共聚物与低门尼黏度部分的乙丙共聚物的重均相对分子质量比为10~15;通过调节高门尼黏度部分的乙丙共聚物与低门尼黏度部分的乙丙共聚物的掺混比例,最终合成的乙丙聚合物与国外产品指标相当。Using dichloro(ethoxy)oxovanadium(Vx) as the main catalyst,ethylaluminium sesquichloride(AQ) as the co-catalyst,ethylene and propylene as the polymerization monomers,and ethylene norbornene(ENB) as the third monomer,in hexane,the high and low Mooney viscosity ethylene-propylene-diene copolymer were synthesized by homogeneous polymerization.High molecular weight partial ethylene-propylene copolymer and low molecular weight partial ethylene-propylene copolymer were mixed together in proportion.The high molecular weight partial ethylene-propylene copolymer had a high ethylene content and low ENB content.The low molecular weight partial ethylene-propylene copolymer had a low ethylene content and high ENB content.The mass average molecular weight ratio of the high and low Mooney viscosity ethylene-propylene copolymer was 10~15.By adjusting the mixing ratio,the products with better performance were finally synthesized.

关 键 词：乙丙橡胶 掺混 门尼黏度 合成 

分 类 号：TQ333.4[化学工程—橡胶工业]