Hydrothermal Synthesis of Zn2SnO4/Few-Layer Boron Nitride Nanosheets Hybrids as a Visible-Light-Driven Photocatalyst  

作　　者：WANG Yijin WU Xiangfeng 王一瑾;吴湘锋;ZHAO Zehua;LI Hui;ZHANG Chenxu;SU Junzhang;ZHANG Jiarui;CAO Zuolin;WANG Yiwei;WANG Kaiyuan;PAN Juncheng(School of Materials Science and Engineering,Hebei Provincial Key Laboratory of Traffic Engineering Materials,Shijiazhuang Tiedao University)

机构地区：[1]School of Materials Science and Engineering,Hebei Provincial Key Laboratory of Traffic Engineering Materials,Shijiazhuang Tiedao University

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2019年第3期563-567,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by Natural Science Foundation of Hebei Province,China(No.E2013210011)

摘　　要：Zn2SnO4/few-layer boron nitride nanosheets (FBNNS) hybrids were synthesized via a one-step hydrothermal method. The structures, morphology, optical properties, electron transformation and separation of the as-prepared products were characterized by X-ray diffraction, transmission electrical microscopy, UV-vis diffuse reflectance spectroscopy and electrochemical impedance spectroscopy, respectively. Rhodamine B was used to evaluate the photocatalytic activities of the as-prepared samples under visible light illumination. The photocatalytic mechanism was also explored. Experimental results showed that the degradation efficiency of rhodamine B was firstly increased and then decreased with increasing the usage amount of FBNNS. When it was 9 wt% based on the weight of Zn2SnO4, the degradation efficiency of the as-prepared Zn2SnO4/FBNNS-9 wt% composites reached to the maximum of 97.5 % in 180 min, which was higher than 39.2 % of pure Zn2SnO4. Moreover, the holes played mainly active roles in photocatalytic reaction process. In addition, the as-prepared hybrids could enhance the separation efficiency of photoexcited carriers compared to pure Zn2SnO4.Zn2SnO4/few-layer boron nitride nanosheets（FBNNS） hybrids were synthesized via a one-step hydrothermal method. The structures, morphology, optical properties, electron transformation and separation of the as-prepared products were characterized by X-ray diffraction, transmission electrical microscopy, UV-vis diffuse reflectance spectroscopy and electrochemical impedance spectroscopy, respectively. Rhodamine B was used to evaluate the photocatalytic activities of the as-prepared samples under visible light illumination. The photocatalytic mechanism was also explored. Experimental results showed that the degradation efficiency of rhodamine B was firstly increased and then decreased with increasing the usage amount of FBNNS. When it was 9 wt% based on the weight of Zn2 SnO4, the degradation efficiency of the as-prepared Zn2 SnO4/FBNNS-9 wt% composites reached to the maximum of 97.5 % in 180 min, which was higher than 39.2 % of pure Zn2 SnO4. Moreover, the holes played mainly active roles in photocatalytic reaction process. In addition, the as-prepared hybrids could enhance the separation efficiency of photoexcited carriers compared to pure Zn2 SnO4.

关 键 词：zinc STANNATE boron NITRIDE NANOSHEETS photocatalysis 

分 类 号：TB[一般工业技术]