轻质碳酸镁改性钢结构防火卷材研究  

Study on the steel structure fireproof coil modified by light magnesium carbonate

作　　者：杨守生 罗敏捷 周俊伟 牛贵来 牛少伟 孟涛 YANG Shou-sheng;LUO Ming-jie;ZHOU Jun-wei;NIU Gui-lai;NIU Shao-wei;MENG Tao(China People's Police University,Hebei Lang fang 065000,China;Zhumadian Fire Detachment,Henan Zhumadian 463000,China;Puyang Fire Detachment,Henan Puyang 457000,China)

机构地区：[1]中国人民警察大学,河北廊坊065000 [2]驻马店市消防支队,河南驻马店463000 [3]濮阳市消防支队,河南濮阳457000

出　　处：《消防科学与技术》2019年第5期674-676,共3页Fire Science and Technology

基　　金：河北省科技计划项目(17211504)

摘　　要：为改善CPE/EPDM基钢结构防火卷材的防火保护性能,利用轻质碳酸镁对其进行改性处理。将阻燃剂、LMC与树脂混合,经开放式炼胶机混炼均匀形成胚材,利用平板硫化剂热压成型得到样品,对样品的燃烧性能和耐火性能进行研究。结果表明:轻质碳酸镁改性CPE/EPDM基钢结构防火卷材的极限氧指数提高16.7%,水平燃烧性能达到FH-1,垂直燃烧等级由FV-1提升为FV-0,最大烟密度降低24.5%,烟密度等级从68.20降为40.41;添加15.0%轻质碳酸镁的卷材耐火极限增加18.4%。轻质碳酸镁有效提高了防火卷材的阻燃防火性能,且具有抑烟作用,耐火极限提升明显。In order to improve the fire protection performance of CPE/EPDM base steel structure fireproofing coil,light magnesium carbonate was used on the modification.The flame retardant,LMC and resin was blended evenly to form embryo material by open rubber mixer.Samples were obtained by hot pressing with flat vulcanizing agent.The combustion characteristics and flame retardancy properties of the sample were studied.The results showed that the limit oxygen index of light magnesium carbonate modified CPE/EPDM base steel structure fireproofing coil was increased by16.7%,the horizontal combustion performance was FH-1,the vertical burning level was promoted from FV-1 to FV-0,the greatest smoky density was reduced by 24.5%,and the smoke density rank was reduced from 68.20 to 40.41;The fireproof limit of rolled material with 15.0%light magnesium carbonate was increased by18.4%.The light magnesium carbonate has effectively improved the fire retardant properties of the fire resistant rolling material and has the function of smoke suppression,and the fire retardant limit has been significantly improved.

关 键 词：轻质碳酸镁 防火卷材 耐火极限 氯化聚乙烯 三元乙丙橡胶 