Preparation of a Novel Cationic Photosensitive Resin(3D-SLR01) for Stereolithography 3D Printing and Determination of Its Some Properties  

作　　者：HUANG Biwu WU Baolin HAN Linlin LU Zhenting ZHOU Wenbin 黄笔武;WU Baolin;HAN Linlin;LU Zhenting;ZHOU Wenbin(School of Materials Science and Engineering, Nanchang University)

机构地区：[1]School of Materials Science and Engineering, Nanchang University

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2019年第4期761-768,共8页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China(No.51563017)

摘　　要：A novel cationic photosensitive resin(3 DSLR-01) for stereolithography 3 D printing was prepared with 3,4-epoxycyclohexylmethyl-3’,4’-epoxycyclohexane carboxylate(2021 P),1,4-cyclohexanedimethanol glycidyl ether(JX-026), diglycidyl 4,5-epoxycyclohexane-1,2-dicarboxylate(S-186), polycaprolactone polyol(Polyol-0305), novolac epoxy resin(F-51), bis(3-ethyl-3-oxetanylmethyl) ether(S-221) and a mixture of triarylsulfonium hexafluoroantimonate salts solution(UVI-6976). The properties of the photosensitive resin and its UV-cured films were investigated by some instruments and equipment.The experimental results show that the critical exposure(Ec) of the photosensitive resin is 16.3 mJ/cm^2, the penetration depth(Dp) is 0.14 mm, and the optical property of the photosensitive resin is excellent. Rectangle plates were printed by using a stereolithography apparatus(HRPL-150 A) with the photosensitive resin as the manufacturing material, and the shrinkage rates of the plates were less than 0.60%, which showed that the accuracy of the manufactured plates was very high.A novel cationic photosensitive resin(3 DSLR-01) for stereolithography 3 D printing was prepared with 3,4-epoxycyclohexylmethyl-3’,4’-epoxycyclohexane carboxylate(2021 P),1,4-cyclohexanedimethanol glycidyl ether(JX-026), diglycidyl 4,5-epoxycyclohexane-1,2-dicarboxylate(S-186), polycaprolactone polyol(Polyol-0305), novolac epoxy resin(F-51), bis(3-ethyl-3-oxetanylmethyl) ether(S-221) and a mixture of triarylsulfonium hexafluoroantimonate salts solution(UVI-6976). The properties of the photosensitive resin and its UV-cured films were investigated by some instruments and equipment.The experimental results show that the critical exposure(Ec) of the photosensitive resin is 16.3 mJ/cm^2, the penetration depth(D_p) is 0.14 mm, and the optical property of the photosensitive resin is excellent. Rectangle plates were printed by using a stereolithography apparatus(HRPL-150 A) with the photosensitive resin as the manufacturing material, and the shrinkage rates of the plates were less than 0.60%, which showed that the accuracy of the manufactured plates was very high.

关 键 词：STEREOLITHOGRAPHY PHOTOSENSITIVE RESIN 3D PRINTING laser 

分 类 号：TB[一般工业技术]