黄土基内墙乳胶漆的制备及性能研究  

Study on Preparation and Performance of Loess-Based Interior Latex Paint

作　　者：韩明虎[1] 胡浩斌[1] 张腊腊[1] 芦娅妮 李永锐 陈水强 Han Minghu;Hu Haobin;Zhang Lala;Lu Yani;Li Yongrui;Chen Shuiqiang(College of Chemistry and Chemical Engineering,Longdong University,Qingyang,Gansu 745000,China;Qingyang Xiqing coating Co.,Ltd.,Qingyang,Gansu 745000,China)

机构地区：[1]陇东学院化学化工学院,甘肃庆阳745000 [2]庆阳西庆涂料有限公司,甘肃庆阳745000

出　　处：《涂料工业》2019年第11期51-55,共5页Paint & Coatings Industry

基　　金：甘肃省高等学校科研成果转化项目(2017D-22)

摘　　要：以黄土为基料,通过改性、乳化、分散制备生态型内墙乳胶漆。以内墙乳胶漆的主要性能为指标,采用单因素控制变量法优化黄土改性工艺(用量、煅烧温度及时间)与乳胶漆配方。结果表明:450℃恒温煅烧90 min的黄土,添加量为15%时制备的乳胶漆各项性能最佳。产品完全符合且优于《合成树脂乳液内墙涂料》(GB/T9756-2009)要求,成本低、工艺简单和绿色环保,有良好的实际应用前景。Using loess as the base material,the ecological interior wall latex paint was prepared by modification,emulsification and dispersion processes. Taking the main performance of theinteriorlatex paint as an indicator,the single factor controlled variable approach was used to optimize the loess modification process(dosage,calcination temperature and time)and the formulation of latex paint. The results showed that the latex paint prepared by incorporation of calcinated loess at 15% on total formulaion,which was calcinated at 450 ℃for 90 minutes at constant temperature,provided the best properties. The product was fully in line with and superior to the requirements instandard of"synthetic resin interior wall latex coatings(GB/T9756-2009)". It was characterized by its low cost,simple technology,environmental friendly,and good practical application prospects.

关 键 词：黄土 改性 单因素控制变量法 内墙乳胶漆 

分 类 号：TQ635.52[化学工程—精细化工]