Mesoporous ZSM-5 Crystals Synthesized by a Novel Amphiphilic Organosilane Soft Template  

作　　者：WANG Yumin LIU Dongliang 王毓敏;刘栋良(Department of Applied Chemistry, College of Chemistry, Chemical Engineering and Biotechnology, Donghua University)

机构地区：[1]Department of Applied Chemistry, College of Chemistry, Chemical Engineering and Biotechnology, Donghua University

出　　处：《Journal of Donghua University(English Edition)》2019年第4期340-343,共4页东华大学学报（英文版）

基　　金：National Natural Science Foundation of China(No.21676053)

摘　　要：Hierarchical ZSM-5 zeolite was hydrothermally synthesized by a novel silicone quaternary ammonium salt surfactant as a mesopore director.The crystallinity and the morphology of sample were characterized by X-ray diffraction(XRD),field-emission scanning electron microscope(FE-SEM),and transmission electronic microscope(TEM).Results indicated that the prepared ZSM-5 zeolites had good crystallinity,ellipsoid structure morphology and rough surface.Moreover,the pore size was enlarged to about 4 nm measured by nitrogen sorption,which indicated positive function of the synthesized template.Hierarchical ZSM-5 zeolite was hydrothermally synthesized by a novel silicone quaternary ammonium salt surfactant as a mesopore director. The crystallinity and the morphology of sample were characterized by X-ray diffraction(XRD), field-emission scanning electron microscope(FE-SEM), and transmission electronic microscope(TEM). Results indicated that the prepared ZSM-5 zeolites had good crystallinity, ellipsoid structure morphology and rough surface. Moreover, the pore size was enlarged to about 4 nm measured by nitrogen sorption, which indicated positive function of the synthesized template.

关 键 词：hierarchical PORE ZSM-5 ZEOLITE soft TEMPLATE ORGANOSILANE 