氧化锆球体表面机械球磨涂覆钛涂层工艺研究  

Study on the preparation process of Ti coatings on ZrO2 balls by mechanical milling coating technology

作　　者：吴开霞[1] 查五生[2] 唐鑫鑫 张少鹏 WU Kai-xia;ZHA Wu-sheng;TANG Xin-xin;ZHANG Shao-peng(College of Intelligent Manufacturing,Jincheng Collegeof Sichuan University,Chengdu 611731,China;School of Materials Science and Engineering,XihuaUniversity,Chengdu 610039,China;Chengdu Branch of Zigong Cemented Carbide Corp.Ltd.,Chengdu 610100,China)

机构地区：[1]四川大学锦城学院智能制造学院,成都611731 [2]西华大学材料科学与工程学院,成都610039 [3]自贡硬质合金有限责任公司成都分公司,成都610100

出　　处：《粉末冶金技术》2019年第6期444-450,共7页Powder Metallurgy Technology

基　　金：四川省科技计划资助项目(2014GZ0088)

摘　　要：采用机械球磨涂覆技术在1mm氧化锆球体上制备钛涂层,研究了球料比、球磨时间及球磨气氛对钛涂层形成的影响,利用扫描电子显微镜(scanning electron microscope,SEM)、X射线衍射(X-ray diffraction,XRD)及超声波对钛涂层的显微结构及物理性能进行了表征。结果表明,钛涂层厚度随球磨时间、球料比的增加先增加后减小,球磨30 h的涂层平均厚度最大,约为76μm,球料比2.5:1.0的涂层平均厚度最大,约为73μm;钛涂层结合强度随球磨时间的增加先增加后减小;球磨过程中适当增加球料比,可缩短涂层的形成时间;在球磨过程中间歇性引入空气,球磨罐中的钛粉易被氧化成TiO,导致涂层形成困难,故而球磨过程处于密封状态更有利于钛涂层的形成。The titanium(Ti) coatings were prepared on the surface of ZrO2 balls in the average diameter of 1 mm by mechanical milling coating technology. The influences of milling time, ball-to-powder weight ratio, and milling atmosphere on the formation of titanium coatings were systemically investigated. The microstructure and physical properties of titanium coatings were characterized by scanning electron microscope(SEM), X-ray diffraction(XRD), and ultrasonic wave. The results show that, the thickness of titanium coatings firstly increases and then decreases with the increasing of milling time and ball-to-powder weight ratio. The average thickness of the coating milled for 30 h reaches the maximum as about 76 μm. Meanwhile, the ball-to-powder weight ratio of 2.5:1.0 can provide the maximum average thickness of Ti coatings(about 73 μm). The binding strength of titanium coating increases first and then decreases with the increasing of milling time. The forming time of coatings can be shortened by increasing the ball-to-powder weight ratio properly. The titanium powders in the ball-mill can be easilty oxidized to TiO by the intermittent air introduction, which further hinders the formation of coatings. So, the sealing state in ball milling process is more beneficial to the formation of titanium coating.

关 键 词：钛涂层 机械球磨涂覆技术 球磨时间 球料比 球磨气氛 

分 类 号：TB43[一般工业技术]