水滑石对MCA阻燃PA6性能的影响  

Effect of Hydrotalcite on the Properties of MCA/PA6 Flame-Retardant Composites

作　　者：杨海民 李函坚 林经萍 刘鹏辉 张宗豪 陈新泰 吕伟 YANG Hai-min;LI Han-jian;LIN Jing-ping;LIU Peng-hui;ZHANG Zong-hao;CHEN Xin-tai;LU Wei(Polyrocks Chemocal Co.,Ltd.,Qingyuan 511540,China)

机构地区：[1]广东聚石化学股份有限公司

出　　处：《塑料工业》2020年第1期96-99,共4页China Plastics Industry

摘　　要：研究了水滑石对三聚氰胺氰尿酸盐(MCA)阻燃聚酰胺(PA6)的力学性能、热稳定性和阻燃性能的影响,讨论了水滑石在MCA阻燃PA6热分解历程和燃烧过程所发挥的作用。结果表明,随着水滑石用量从0%增加到15%,MCA阻燃PA6复合材料的拉伸强度从73 MPa下降到65 MPa,降幅约11%,冲击强度从40 J/m下降到34 J/m,降幅为15%。随着水滑石用量增加,MCA阻燃PA6的复合材料的热稳定性能下降,但材料的防火性能得到提高,另外,随着水滑石用量从0%增加到15%,M CA阻燃PA6的极限氧指数从32%升高到36%。The mechenical properties,thermal stability and flame retardent property of melamine cyanurate(MCA)/polyamide 6(PA6) composites containing hydrotalcite were studied.The effects of hydrotalcite on the flame retardant PA6 thermal decomposition and combustion process were discussed.The results show that the tensile strength of MCA/PA6 composites decreases from 73 MPa to 65 MPa,the impact strength decreases from 40 J/m to 34 J/m with hydrotalcite content increasing from 0 to 15%.The thermal property of MCA/PA6 fire-retardant composites could decrease with the increasing of hydrotalcite content,but the fire resistance is increased.Otherwise,with hydrotalcite content increasing from 0 to 15%,the oxygen index of the composite increases from 32%to 36%.

关 键 词：水滑石 三聚氰胺氰尿酸盐 阻燃聚酰胺复合材料 

分 类 号：TQ323.6[化学工程—合成树脂塑料工业]