Reduction kinetics of MgO-doped calcium ferrites under CO-N2 atmosphere  

作　　者：Tian-xiong Wang Cheng-yi Ding Xue-wei Lv Sen-wei Xuan Gang Li 

机构地区：[1]Chongqing Key Laboratory of Vanadium-Titanium Metallurgy and New Materials,Chongqing University,Chongqing 400044,China [2]School of Materials Science and Engineering,Chongqing University,Chongqing 400044,China

出　　处：《Journal of Iron and Steel Research International》2019年第12期1265-1272,共8页

基　　金：the financial support of the National Natural Science Foundation of China(51234010 and 51522403);the Program for New Century Excellent Talents in University and the Program for the Youth Top-Notch Talents of Chongqing(20151001);Ultrasonic Assisted Iron Ore Sintering Technology Research(cstc2014kjrc-qnrc90001),and China Scholarship Council.

摘　　要：The effect of magnesia on calcium ferrite(CaO.Fe2O3)reduction by CO was examined by isothermal thermogravimetry.Samples of calcium ferrite added with 0,2,4,and 8 wt.%magnesia(abbreviated as CF,CF2M,CF4M,and CF8M)were prepared.Phase composition was analyzed by X-ray diffraction,and the results indicated that CF2M and CF4M are reduced to lower reduction degree and with lower apparent activation energy than CF;and CF8M with more MgO.Fe2O3 is reduced to a lower degree and with more difficulty compared with CF.Reduction rate analysis revealed that CF,CF2M,CF4M,and CF8M reductions are all typical two-step reactions with the order of CF→CWF(CaO.FeO.Fe2O3)→Fe.The apparent reduction activation energies of CF,CF2M,CF4M,and CF8M are 46.89,37.30,17.30,and 29.20 kJ/mol,respectively.Sharp analysis depicted that CF2M,CF4M,and CF8M reductions are all described by 2D Avrami–Erofeev(A–E)equation(A2)in the whole process,while CF reduction is first expressed by A2 and then by 3D A–E equation(A3).Different from shrinking core model,a new kinetic model for powdery samples reduction was proposed to illustrate the relationship among reduction rates,reduction routes,and model functions.

关 键 词：Calcium ferrite MAGNESIA Reduction kinetics Reduction model 

分 类 号：TG1[金属学及工艺—金属学]