涤纶莫代尔交织物的工艺设计与生产  

Design and Production of Polyester and Modal Intertexture Fabric

作　　者：王金玉 WANG Jin-yu(Nanjing Customs Industrial Products Testing Center,Wuxi 214021,China)

机构地区：[1]南京海关纺织工业产品检测中心,江苏无锡214021

出　　处：《纺织科技进展》2020年第4期31-32,36,共3页Progress in Textile Science & Technology

摘　　要：经丝使用涤纶长丝,纬纱使用莫代尔,生产出的织物强力高,吸湿性、耐磨性、尺寸稳定性好,织物的手感特别滑爽,布面光泽亮丽。络丝采用“低速度、小张力”为工艺原则,络丝速度120m/min,络丝张力5cN;整经采用“中车速、中张力、卷绕均匀”的工艺原则,整经速度550m/min左右,整经张力控制在15cN,整经配轴为960根×3轴+959根×4轴;浆丝以“中车速、保伸长、重被覆”为工艺原则,上浆时要加强纤维之间的抱合,同时加入抗静电剂减少静电产生;并轴以“中车速、匀张力”为工艺原则,相对湿度要偏大控制,以减少静电的产生;织造以“高车速、早开口、高后梁、大张力”为工艺原则,车速600r/min,上机张力为2200N。开口时间290°,后梁高度为+1。Polyester filament was used for warp yarn and modal was used for weft yarn.The produced fabric hadhigh strength,good moisture absorption,wear resistance,dimensional stability,smooth touch and glossy appearance.The winding process was based on the principle of“lower speed,lower tension”,the speed was 120 m/min and thewinding tension was 15 cN.The warping process was based on the principle of“nedium speed,medium tension,uniform”,the speed was 550 m/min,the warping tension was 15 cN,and the warping axles were 960×3+959×4/The sizing process was based on the principle of“medium speed,keeping elongation and covering again”,It was necessary to strengthen the bonding between fibers,and add antistatic agent to reduce the generation of static electricity;The re-beaming was based on the technological principle of“medium speed anduniform tension”,and the relative humidity should be controlled to reduce the generation of static electricity;The weaving was based on the technological principle of“high speed,early opening,high back beam and large tension”,the speed was 600 r/min and the loom tension was 2200 N.The opening timewas 290°and the height of the rear beam was+1.

关 键 词：涤纶长丝 莫代尔 平纹地小提花组织 浆丝 

分 类 号：TS155.6[轻工技术与工程—纺织材料与纺织品设计]