火焰喷淬制备BaO-TiO2和La2O3-Nb2O5玻璃微球及性能研究  

Synthesis of Amorphous BaO-TiO2 and La2O3-Nb2O5 Glass Microspheres Using Containerless Flame-Spraying Technique and Their Properties

作　　者：张英 马晓光[1] 李晓禹[1,2] 李建强 李江涛[3] 贺刚 Zhang Ying;Ma Xiaoguang;Li Xiaoyu;Li Jianqiang;Li Jiangtao;He Gang(National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology,CAS Key Laboratory of Green Process and Engineering,Institute of Process Engineering,Chinese Academy of Sciences,Beijing 100190,China;University of Chinese Academy of Sciences,Beijing 100049,China;Key Laboratory of Cryogenics,Technical Institute of Physics and Chemistry,Chinese Academy of Sciences,Beijing 100190,China)

机构地区：[1]中国科学院过程工程研究所湿法冶金清洁生产技术国家工程实验室中国科学院绿色过程与工程重点实验室,北京100190 [2]中国科学院大学,北京100049 [3]中国科学院理化技术研究所低温工程学重点实验室,北京100190

出　　处：《稀有金属材料与工程》2020年第2期482-486,共5页Rare Metal Materials and Engineering

基　　金：National Natural Science Foundation of China(51671181,51674232,51471158,51432004)。

摘　　要：分别以BaO、TiO2和La2O3、Nb2O5为原料采用火焰喷淬法制备了不含网络形成体的BaTi2O5(BTO)和35La2O3-65Nb2O5 (LNO)玻璃微球。结果表明,所有BTO为透明的、表面光滑、无结晶痕迹的玻璃微球,粒径分布集中在8~40μm,且具有较低的非晶形成能力;而大部分的LNO为透明的、具有光滑表面的玻璃微球,粒径分布集中在10~40μm,少量粒径较大的LNO微球表面粗糙,存在微米级LaNbO4和LaNb3O9晶粒。计算结果显示,BTO和LNO玻璃微球均具有高折射率,分别为2.20和2.23,是非常有应用前景的窗口、镜头以及反光标志膜材料。The BaTi2O5(BTO) and 35La2O3-65Nb2O5(LNO) amorphous microspheres without conventional network-forming oxides were fabricated by a containerless flame-spraying technique.The results show that transparent BTO and LNO glass microspheres were successfully prepared.All the BTO glass microspheres have smooth surfaces and no crystalline traces,indicating they are amorphous glass.Their diameters range from 8μm to 40μm.And their amorphous forming ability is low.Most of the LNO glass microspheres have diameters of 10μm to 40μm,which are amorphous glass with smooth surfaces.And a small number of LNO microspheres have large particle diameters,which possess micron-sized grains on their surfaces.The BTO and LNO glass microspheres have high refractive index of 2.20 and 2.23,respectively,which are very promising to be applied as window,lens and reflection film materials.

关 键 词：火焰喷淬 玻璃微球 TiO2基玻璃 Nb2O5基玻璃 

分 类 号：TQ171.1[化学工程—玻璃工业]