Preparation and Characterization of Natural Bamboo Fiber  

作　　者：Kaixuan Li Qingxian Miao He Zhao Jiawei Yang Haitao Cheng Lihui Chen 

机构地区：[1]College of Material Engineering,Fujian Agriculture and Forestry University,Fuzhou,Fujian Province,350100,China [2]International Centre For Bamboo and Rattan,Beijing,100102,China

出　　处：《Paper And Biomaterials》2020年第2期43-52,共10页造纸与生物质材料（英文）

基　　金：financially supported by the National Key R&D Program of China(2017YFD0600802).

摘　　要：In this study,natural bamboo fiber was prepared combining chemical pretreatment with mechanical disc refining,opening,and carding.An orthogonal experiment was designed based on four factors and three levels;thereafter,the manufacturing process was optimized.The length,diameter,tensile strength,and elastic modulus of the bamboo fiber were determined,and the crystallinity and morphology of the fiber were analyzed using X-ray diffraction(XRD)and scanning electron microscopy(SEM).The results showed that the optimum parameters for the chemical pretreatment were a cooking temperature of 130℃,heating time of 2 h,NaOH dosage of 2%,and Na2SO3 dosage of 10%.The cooking yield of bamboo chips was 89.5%,and the carding yield of natural bamboo fiber was 43.0% under the optimum conditions.The length,diameter,tensile strength,and elastic modulus of the obtained fiber were 36.71 mm,0.285 mm,407 MPa,and 27.7 GPa,respectively.XRD analysis and SEM observations showed that the technology used in this study can produce bright and compact natural bamboo fibers with high crystallinity.

关 键 词：natural BAMBOO fiber chemical PRETREATMENT DISC REFINING sulfonic ACID group YIELD 

分 类 号：TQ340.1[化学工程—化纤工业]