涤纶织物上自交联型P(St-NMA)光子晶体的构筑及其结构稳固性  

Preparation and stability of self-crosslinking P( St-NMA) photonic crystals with structural colors on polyester fabrics

作　　者：刘国金[1,2] 韩朋帅 柴丽琴 吴钰 李慧 高雅芳 周岚[3] LIU Guojin;HAN Pengshuai;CHAI Liqin;WU Yu;LI Hui;GAO Yafang;ZHOU Lan(Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology,Zhejiang Sci-Tech University,Hangzhou,Zhejiang 310018,China;Key Laboratory of Advanced Textile Materials and Manufacturing Technology,Ministry of Education,Zhejiang Sci-Tech University,Hangzhou,Zhejiang 310018,China;Engineering Research Center for Eco-Dyeing and Finishing of Textiles,Ministry of Education,Zhejiang Sci-Tech University,Hangzhou,Zhejiang 310018,China)

机构地区：[1]浙江理工大学浙江省纤维材料和加工技术研究重点实验室,浙江杭州310018 [2]浙江理工大学先进纺织材料与制备技术教育部重点实验室,浙江杭州310018 [3]浙江理工大学生态染整技术教育部工程研究中心,浙江杭州310018

出　　处：《纺织学报》2020年第5期99-104,共6页Journal of Textile Research

基　　金：浙江省自然科学基金项目(LQ19E030022,LY20E030006);浙江省基础公益研究计划项目(LGC20E030001)。

摘　　要：为提升光子晶体生色结构在纺织基材上的稳固性,以自交联型聚(苯乙烯-N-羟甲基丙烯酰胺)(P(StNMA))胶体微球为结构基元,通过数码喷印技术将其施加到涤纶织物上构筑光子晶体生色结构。观测P (StNMA)微球的形貌,表征光子晶体的排列和结构色效果,并测试和对比PSt和P(St-NMA) 2种光子晶体生色结构在基材上的稳固性。结果表明:P(St-NMA)胶体微球具有典型的核壳结构,其中疏水性的聚苯乙烯(PSt)为核层,亲水性的聚N-羟甲基丙烯酰胺为壳层;P(St-NMA)光子晶体生色结构排列规整,色彩鲜艳、虹彩明显;相比PSt光子晶体生色结构,P(St-NMA)光子晶体生色结构的稳固性显著提升,经折叠、水洗后不易脱落。In order to improve the stability of photonic crystals with structural colors on textile substrates,the poly( styrene-N-methylol acrylamide)( P( St-NMA)) colloidal microspheres with self-crosslinking were used as structural units to fabricate photonic crystals on polyester fabrics by a digital printing technology. The morphology of P( St-NMA) microspheres was observed,the arrangement and structural color effects of prepared photonic crystals were deeply characterized,and the stability of the P( St-NMA)photonic crystals with structural colors on the substrate was tested and compared with pure PSt photonic crystals. The results show that the P( St-NMA) colloidal microspheres present a typical core-shell structure,in which the hydrophobic PSt actes as the core layer and the hydrophilic PNMA as the shell layer. The prepared P( St-NMA) photonic crystals present regular arrangement,bright structural colors and obvious iridescence. Compared with pure PSt photonic crystals,the stability of P( St-NMA) photonic crystals is significantly improved,and P( St-NMA) photonic crystals are not easy to fall off the substrate surface after folding and washing. The improvement of the stability is attributed to the self-crosslinking between adjacent microspheres,which improves the bonding force between each other and enhances the bonding fastness between the photonic crystal layers and the substrates some extent.

关 键 词：自交联 P(St-NMA)胶体微球 光子晶体 生色结构 涤纶织物 