作 者:王垒 刘中华 张伟 赵英建 苏英强 曾祥文 俞奇效 刘锟[3] WANG Lei;LIU Zhonghua;ZHANG Wei;ZHAO Yingjian;SU Yingqiang;ZENG Xiangwen;YU Qixiao;LIU Kun(ZHE JIANG JINGGONG STEEL BUILDING CONSTRUCTION GROUP Co.,Ltd.,Shaoxing 312030,China;Shanghai building space structure engineering technology research center,Shanghai 00041,China;Shougang Technology Research Institute,Beijing 100043,China)
机构地区:[1]浙江精工钢结构集团有限公司,浙江绍兴312030 [2]上海建筑空间结构工程技术研究中心,上海200041 [3]首钢技术研究院,北京100043
出 处:《电焊机》2020年第5期27-30,I0006,共5页Electric Welding Machine
基 金:国家重点研发计划项目(2017YFB0304700和2017YFB0304702);上海市科委“上海建筑空间结构工程技术研究中心”项目(14DZ2252300)。
摘 要:通过焊接性试验对28 mm厚的新钢种SQ460FRW抗震耐蚀耐火钢进行焊接工艺研究。改善了焊接坡口,对比纯CO2和混合气体保护下对接平焊的差异,对气保焊对接接头平焊、立焊、横焊、仰焊和十字接头横焊、立焊进行了工艺评定。在十字接头中应用了双面双弧单熔池同步同向焊接、高速脉冲压缩电弧技术、双面K型坡口35°+4 mm间隙等焊接方法,焊缝无损检测、力学性能检测、宏观金相、冲击试验、微观金相组织观察等各项检测内容均合格,可用于指导后续新钢种的实际应用。In this paper,the welding technology,mechanics and chemistry of the new steel type SQ460FRW with 28 mm thickness were studied on the basis of welding test,and the welding slope was improved.The differences between pure CO2 and hybrid gas under the protection of butt flat welding were compared.The process evaluation of flat welding,vertical welding,horizontal welding,vertical welding and cross welding of gas welding joints was carried out.Welding methods,such as simultaneous welding of double-sided double-arc single melting pool,high-speed pulse compression arc technology,and double-sided K-shaped slope 35°+4 mm gap,have been applied in the cross joints.Weld non-destructive testing,mechanical performance testing,macroscopic metallography,different temperature impact test,microscopic metallographic tissue observation and other test content are all qualified,can be used to guide the practical use of subsequent new steel species.
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在链接到云南高校图书馆文献保障联盟下载...
云南高校图书馆联盟文献共享服务平台 版权所有©
您的IP:216.73.216.120