硅酸盐胶黏剂在高温磨蚀条件下的退化行为  被引量:1

Degradation of Silicate Adhesive Under High Temperature andTribo-Corrosion Condition

在线阅读下载全文

作  者:赵宇航 王永旺 ZHAO Yuhang;WANG Yongwang(Research Center of Shenhua Zhunneng Comprehensive Resource Development Co.Ltd.,Ordos 010300,China)

机构地区:[1]神华准能资源综合开发有限公司研发中心,鄂尔多斯010300

出  处:《材料导报》2020年第S01期181-184,共4页Materials Reports

基  金:国家科技部“十二五”科技支撑计划项目(2011BAA04B05)。

摘  要:本工作设计并制备了含K^+、Na^+的液相硅酸盐胶泥,通过模拟高温磨蚀的特殊工况,采用微观结构扫描、XRD物相测试、力学压缩试验及ANSYS受力分析研究了该胶泥的退化行为。结果表明:在高温磨损工况下(温度200℃,流速2 m/s),试样表面形成胶凝状的难溶性混合盐,强度退化率为12%;在高温腐蚀(200℃,31%盐酸溶液)及高温腐蚀磨损(200℃,31%盐酸溶液、流速2 m/s)条件下,胶体表面发生化学腐蚀,生成可溶解性盐及氯化物,未形成有效的保护膜,其强度退化率分别为31%与39%。在本试验条件下,硅酸盐胶黏剂在高温磨蚀条件下的损伤主要受腐蚀因素控制。The silicate adhesive with liquid phase containing K+,Na+was designed and prepared,and the properties were studied under special high temperature and tribo-corrosion working conditions.The degradation behavior of the adhesive was evaluated and analyzed through scanning electron microscopic,X-ray diffraction(XRD)test,mechanical compression test and finite element modeling.The results showed that the insoluble mixed-salt formed on the surface of the adhesive under high temperature and abrasion condition(with a temperature of 200℃and flow rate of 2 m/s).The degradation rate of strength was about 12%.Both under high temperature corrosion condition(200℃,solution with 31%hydrochloric acid)and high temperature tribo-corrosion condition(200℃,solution with 31%hydrochloric acid and flow rate of 2 m/s),the chemical reaction occurred on the surface of adhesive and the soluble salt with chloride was generated,which cannot form protective film.The degradation rates of strength are 31%and 39%respectively under above two conditions.Under high temperature and tribo-corrosion,the damage process of the silicate adhesive was mainly controlled by corrosion factor.

关 键 词:硅酸盐胶黏剂 高温磨蚀 腐蚀 退化行为 有限元分析 

分 类 号:TB321[一般工业技术—材料科学与工程]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象