退火制度对2024铝合金冷轧板材力学性能的影响  

Effect of Annealing on Mechanical Properties of the Cold-rolled Sheet of 2024 Aluminum Alloy

作　　者：梁爽[1] 刘智鑫[1] 赵伟 贾天琦 李宋伟 LIANG Shuang;LIU Zhi-xin;ZHAO Wei;JIA Tian-qi;LI Song-wei(School of Yingkou Institute of Technology,Yingkou 115014,China)

机构地区：[1]营口理工学院,辽宁营口115014

出　　处：《世界有色金属》2020年第5期8-9,共2页World Nonferrous Metals

基　　金：营口理工学院青年项目自然科学(QNL201825);2019营口市企业博士双创计划,热处理工艺对变形铝合金板材组织与性能的影响(QB-2019-09)。

摘　　要：本文对冷轧变形后的2024铝合金板材进行不同的退火处理工艺,退火温度为300℃~440℃之间每隔20℃取一个点,退火保温时间分别为20min、50min、80min、110min,并对退火处理后的合金进行力学性能的对比分析研究。结果表明:退火温度越高,保温时间越长,抗拉强度、屈服强度下降幅度较小,变化不明显,延伸率大幅提高。In this paper,2024 aluminum alloy sheet after cold rolling was annealed with taking one point every 20℃between 300℃~440℃for 20min,50min,80min and 110min respectively.The mechanical properties of the annealed alloy were compared.The results show that the higher the annealing temperature,the longer the holding time,the smaller the decrease of tensile strength and yield strength,and the larger the elongation.

关 键 词：2024合金 冷轧板材 退火 性能 

分 类 号：TG156.2[金属学及工艺—热处理]