Oxide dispersion strengthened stainless steel 316L with superior strength and ductility by selective laser melting  

作　　者：Yuan Zhong Leifeng Liu Ji Zou Xiaodong Li Daqing Cui Zhijian Shen 

机构地区：[1]Department of Materials and Environmental Chemistry,Arrhenius Laboratory,Stockholm University,SE-10691 Stockholm,Sweden [2]School of Metallurgy and Materials,University of Birmingham,B152TT UK [3]Department of Chemistry-Radiochemistry,P.O.Box 55,FI-00014 University of Helsinki,Finland

出　　处：《Journal of Materials Science & Technology》2020年第7期97-105,共9页材料科学技术（英文版）

摘　　要：Dense oxide dispersion strengthened(ODS) 316 L steels with different amount of Y2O3 additions were succe s s fully fabricated by selective laser melting(SLM) even though part of the added Y2O3 got lost during the process.The microstructure was characterized in details and the mechanical properties were tested at room temperature,250℃ and 400℃,respectively.The effect of the scanning speed on agglomeration of nanoparticles during SLM process was discussed.Superior properties,e.g.,yield strength of 574 MPa and elongation of 91%,were achieved at room temperature in SLM ODS 316 L with additional 1% of Y2 O3.At elevated temperature s,the strength kept high but the elongations dropped dra matically.It was observed that nano-voids nucleated throughout the whole gauge section at the sites where nanoinclusions located.The growth and coalescence of these voids were suppre s sed by the formation of an element segregation network before necking,which relieved local stress concentration and thus delayed necking.This unusual necking behavior was studied and compared to the previous theory.It appeared that the strong convection presented in the melt pool can evenly redistribute the short-time milled coarse Y2O3 precursor powder during SLM process.These findings can not only solve the problems encountered during the fabrication of ODS components but also replenish the strengthening mechanism of SLM 316 L thus pave a way for further improving of mechanical properties.

关 键 词：ODS steel Selective laser melting(SLM) Elevated-temperature properties NECKING Strain hardening 