高硬度聚酯酰胺蜡的研发  

Research of High Hardness and Environmental Friendly Polyesteramide Wax

作　　者：满杰 孟祥鹏[2] 陆希峰 刘长城 MAN Jie;MENG Xiang-peng;LU Xi-feng;LIU Chang-cheng(Lunan Institute of Coal Chemical Engineering,Jining 272000,China;Jining Zhongyin Electrochemical Co.,Ltd.,Jining 272000,China;Cooper Tire(Kunshan)Company Ltd.,Kunshan 215331,China)

机构地区：[1]鲁南煤化工研究院,山东济宁272000 [2]济宁中银电化有限公司,山东济宁272000 [3]固铂(昆山)轮胎有限公司,江苏昆山215331

出　　处：《皮革与化工》2020年第3期15-21,共7页Leather And Chemicals

摘　　要：通过直接熔融缩聚法,以十二烷二元酸、1,4-丁二醇、乙醇胺为原料,氧化锌为催化剂,合成出一系列分子量在3000~5100左右的预聚体。以分子量为3300的预聚体为原料,己二酰双己内酰胺为扩链剂,亚磷酸三苯酯为稳定剂,通过扩链反应合成出高硬度的聚酯酰胺蜡。最佳反应条件:扩链剂与预聚体的摩尔比为1.05∶1,反应温度220℃,常压反应时间30 min,减压反应时间1 h。此条件下得白色固体产物,其滴点96℃,针入度0.1(0.1 mm),羟值5.00 mg KOH/g,特性黏度为0.84 dL/g。Using zinc oxide as catalyst,1,12-dodecanedioic acid,1,4-butanediol and ethanolamine as raw material,a series of prepolymers whose molecular weight are between 3000 and 5100 were prepared via direct melt polycondensation reaction.Using prepolymer whose molecular weight is 3300 as raw material,adipoyl biscaprolactamate as chain-extender,triphenyl phosphite as stabilizer,high hardness polyesteramide waxes were prepared via chain-extending reaction.The results showed that the most suitable molar ratio of chain-extender and prepolymer was1.05∶1,the chain-extending reaction temperature was 220℃,the reaction time was 30 min,the press reduction time was 1 h.Under above conditions,the dropping point was 96℃,the hydroxyl value was 5.00 mg KOH/g,the penetration degree was 0.1(0.1mm),and the viscosity was 0.84 dL/g,white solidity.

关 键 词：高硬度 聚酯酰胺蜡 十二烷二元酸 1 4-丁二醇 乙醇胺 

分 类 号：TQ323.6[化学工程—合成树脂塑料工业]