Fe-Zr-M-B(M=Cr,Nb,W)合金系列的热稳定性、微观结构和磁性能研究  

Thermal Property,Microstructure and Magnetic Property of Fe-Zr-M-B(M=Cr,Nb,W)Alloys

作　　者：王晓楠[1,2] 刘洋[2] 左斌[2] WANG Xiaonan;LIU Yang;ZUO Bin(Further education colleges,Jilin Normal University,Siping 136000,Jilin;Key Laboratory of Functional Materials Physics and Chemistry of the Ministry of Education,Jilin Normal University,Changchun 130000,Jilin)

机构地区：[1]吉林师范大学继续教育学院,吉林四平136000 [2]吉林师范大学功能材料物理与化学教育部重点实验室,吉林长春130000

出　　处：《吉林化工学院学报》2020年第5期56-60,74,共6页Journal of Jilin Institute of Chemical Technology

摘　　要：采用单辊快淬法制备Fe91-xZr7Cr2Bx(x=10,12)和Fe81Zr7M2B10(M=Nb,W)非晶合金,并对上述非晶合金进行不同温度热处理.合金的热性能、微观结构及磁性能分别利用X射线衍射仪(XRD)、同步差热分析仪(STA)和振动样品磁强计(VSM)测得.研究表明四种非晶合金的STA中均存在三个晶化放热峰,但初始晶化产物及晶化过程不同,Fe81Zr7Nb2B10非晶合金的初始晶化产物与Fe81Zr7Cr2B10合金相似为单一α-Fe相,Fe81Zr7W2B10非晶合金的初始晶化产物与Fe79Zr7Cr2B12合金相似为α-Fe相和Fe23B6相.不同的晶化产物导致合金的矫顽力(Hc)随热处理温度的变化存在差异,Fe81Zr7Nb2B10合金经热处理后具有较低的矫顽力(Hc).Fe91-xZr7Cr2Bx(x=10,12)and Fe81Zr7M2B10(M=Nb,W)amorphous alloys were prepared by the single roller melt-spinning and isothermally annealed at different temperatures.The thermal stability,microstructure and magnetic property of the alloys were investigated by X-ray diffraction(XRD),simultaneous thermal analysis(STA)and vibrating sample magnetometer(VSM),respectively.Research shows that the four kinds of amorphous alloys all exist three crystallization peaks in the STA curves,but have different crystallization initial products and crystallization processes.The initial crystallization product of Fe81Zr7Nb2B10 amorphous alloy is similar to that of Fe81Zr7Cr2B10 alloy,which is a singleα-Fe phase.The initial crystallization products of Fe81Zr7W2B10 amorphous alloy are similar to those of Fe79Zr7Cr2B12 alloy,which areα-Fe and Fe23B6 phases.The coercivity is different each other along with the change of heat treatment temperature,because of their different crystallization products.Fe81Zr7Nb2B10 alloy has low Hc after heat treatment.

关 键 词：热处理 晶化过程 微观结构 矫顽力 

分 类 号：TG139.8[一般工业技术—材料科学与工程]