硫系、碲系、铅系易切削钢组织及硫化物对比分析  

Structure and sulfide comparative analysis of sulfur,tellurium and lead free-cutting steels

作　　者：曹晨巍 张盼盼 胡绍晖 周蕾 付建勋 CAO Chen-wei;ZHANG Pan-pan;HU Shao-hui;ZHOU Lei;FU Jian-xun(Center for Advanced Solidification Technology (CAST), School of Materials Science and Engineering,State Key Laboratory of Advanced Special Steel, Shanghai University, Shanghai 200444,China;Nanjing Iron and Steel Co., Ltd., Nanjing 210035, China)

机构地区：[1]上海大学材料科学与工程学院先进凝固技术中心,省部共建高品质特殊钢冶金与制备国家重点实验室,上海200444 [2]南京钢铁股份有限公司,江苏南京210035

出　　处：《冶金分析》2020年第7期8-15,共8页Metallurgical Analysis

基　　金：国家自然科学基金(51874195,51671124)。

摘　　要：易切削钢中的夹杂物和组织是影响其切削性能的重要因素,为开发环保型无铅易切削钢,并探究其与含铅易切削钢中组织及硫化物的差异,采用光学显微镜和电子显微镜对1215MS(硫系)、1215Te(碲系)及12L14(铅系)易切削钢中基体组织和硫化物夹杂进行了对比观察与统计分析,结合非水溶液电解法分析了Pb、Te两种元素对钢中夹杂物形貌的影响。结果表明:3种易切削钢基体中组织均为铁素体、珠光体;碲能降低MnS夹杂物长宽比,其长宽比在1~3之间的比例为57%,高于硫系易切削钢1215MS的40%以及铅系易切削钢12L14的33%;碲在易切削钢中生成MnTe,使轧制后的MnS的形貌趋于球状、椭球状、纺锤状,改质作用显著,而铅在易切削钢中以铅单质存在,对硫化物的改质效果有限。The inclusion and structure in free-cutting steel are two important factors influencing the machinability.In order to develop environmental friendly lead-free free-cutting steels,and to explore the difference of structure and sulfide compared to the lead-bearing free-cutting steels,the matrix structure and sulfide inclusions in 1215MS(sulfur),1215Te(tellurium)and 12L14(lead)free-cutting steels were observed and statistically analyzed by optical microscope and electron microscope.The influence of Pb and Te on the inclusion morphology in steel was analyzed by non-aqueous solution electrolysis method.The results showed that the structures of three kinds of free-cutting steels were all composed of ferrite and pearlite.Tellurium could reduce the length-width ratio of MnS inclusions,and the proportion with length-width ratio in range of 1-3 was 57%,which was higher than the 40%of 1215MS and the 33%of 12L14 steel.Tellurium could form MnTe in free-cutting steel,and the morphology of MnS trended to spherical,ellipsoid and spindles after rolling,which had remarkable effect of modification.Lead existed as Pb simple substance in free-cutting steel,which had limited effect on the modification of sulfide.

关 键 词：硫系易切削钢 碲系易切削钢 铅系易切削钢 铁素体 珠光体 MnS-MnTe复合夹杂物 

分 类 号：TF033[冶金工程—冶金物理化学] TF843.5