Multi-stimuli-triggered and self-repairable fluorocarbon organic coatings with urea-formaldehyde microcapsules filled with fluorosilane  

作　　者：Paul CUzoma Fuchun Liu En-Hou Han 

机构地区：[1]Key Laboratory of Nuclear Materials and Safety Assessment,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,110016,China [2]School of Materials Science and Engineering,University of Science and Technology of China,Hefei,230026,China [3]Shenyang Zhongke Engineering Technology Center for Corrosion Control,Shenyang,110016,China [4]Department of Polymer and Textile Engineering,Federal University of Technology,P.M.B.1526,Owerri,Nigeria

出　　处：《Journal of Materials Science & Technology》2020年第10期70-83,共14页材料科学技术（英文版）

基　　金：financial support from the Shenyang Science and Technology Plan Project(Y17-1-039)。

摘　　要：For the purpose of overcoming the lack of durability problems associated with superhydrophobic surfaces which hitherto has limited their use;we prepared multi-stimuli wettability response coatings using a mixture of fluorocarbon resin and urea-formaldehyde microcapsules filled with fluorosilane via interfacial polymerization process.The microcapsules are of good thermal stability and can be triggered to release their core content on exposure to atmospheric conditions resulting in the increase in the water contact angle from 97°to 151°.The prepared coatings gave good adhesion strength,and also showed an increase in the hydrophobic property after undergoing scratch,solvent and UV accelerated aging test.In addition,they offered good self-healing of the hydrophobic property after an initial loss due to alkaline immersion and oxygen plasma etching.The electrochemical measurements revealed a remarkable impedance recovery and suppression of corrosion activities,suggesting them to be a potential candidate material for corrosion protection.

关 键 词：Multi-stimuli MICROCAPSULES Superhydrophobic Self-healing Coatings ANTI-CORROSION 

分 类 号：TQ630.1[化学工程—精细化工]