SUS304DQ精密光亮带钢显微组织及力学性能的研究  

Investigation on Microstructure and Mechanical Properties of SUS304DQ Strip Steel

作　　者：董贤帮 贺超 唐振光 凌锐 DONG Xianbang;HE Chao;TANG Zhenguang;LING Rui(GUANGXI Gulf of Tonkin New Material Co.Ltd.,Beihai 536000,China)

机构地区：[1]广西北部湾新材料有限公司,广西北海536000

出　　处：《材料开发与应用》2020年第3期6-9,共4页Development and Application of Materials

摘　　要：对精密轧制的SUS304DQ带钢光亮退火处理后,观察其宏观表面、微观组织并进行力学性能检测,研究精密轧制后SUS34DQ带钢的退火性能变化。结果表明,钢带在全氢环境中可以有效防止钢带在退火过程中的氧化,减少退火对产品表面质量的影响;厚度为0.3 mm的SUS304DQ精密冷轧带钢的退火温度为1040℃~1160℃,在炉内纯氢气环境下保持3 min,迅速冷却,得到的精密带钢表面质量优良、无瑕疵。Precision rolled SUS304DQ stainless strip steel is bright annealed and the surface,microstructure and mechanicalproperties are investigated to study changes of the properties of the annealed strip steel.Results show that the all hydrogen atmosphere can prevent the oxidation of the strip steel,and reduce the influence of annealing on its surface.When the 0.3 mm thick SUS304DQ stainless strip steel is annealed at 1040~1160℃ for 3 min and then cooled quickly,the strip steel of finesurface quality can be obtained.

关 键 词：不锈精密带钢 SUS304DQ 光亮退火 显微组织 再结晶 

分 类 号：TG142.71[一般工业技术—材料科学与工程]