高阻尼硅橡胶硫化工艺及粘接性能研究  被引量:5

Research of Vulcanization Process and Adhesion Property of High Damping Silicone Rubber

在线阅读下载全文

作  者:肖同亮 穆洪帅 翟继芹 谭莲影[1] 杨瑞蒙[1] 黄良平[1] XIAO Tong-liang;MU Hong-shuai;ZHAI Ji-qin;TAN Lian-ying;YANG Rui-meng;HUANG Liang-ping(Zhuzhou Times New Material Technology Co.,Ltd.,Zhuzhou 412007,China)

机构地区:[1]株洲时代新材料科技股份有限公司,湖南株洲412007

出  处:《特种橡胶制品》2020年第4期27-30,共4页Special Purpose Rubber Products

摘  要:以甲基乙烯基硅橡胶、苯基硅橡胶为原材料制备了高阻尼硅橡胶,研究了硫化工艺、胶粘剂以及偶联剂类型对胶料性能的影响。结果表明,最佳的一段硫化工艺为170℃×T_(c90),二段硫化工艺为220℃×4h;最佳的胶粘剂类型为胶粘剂Primer No.34T,剥离强度达到3MPa以上;最佳的偶联剂类型为γ-氨丙基三乙氧基硅烷,剥离强度达到4.5MPa以上,且破坏发生在橡胶基体内部。The high damping silicone rubber was prepared with methyl vinyl silicone rubber and phenyl silicone rubber,and the influences of vulcanization process,types of adhesives and coupling agents on properties of rubber were studied.The results showed that the comprehensive performance were optimum when the molding process was 170℃×tc90,the post vulcanization process was 220℃×4 h.The peel strength was above 3 MPa when the adhesive was Primer No.34 T.In addition,the peel strength was above 4.5 MPa and adhesion failure occurs inside the rubber matrix when the coupling agent was 3-aminopropyltriethoxysilane.

关 键 词:硅橡胶 硫化工艺 阻尼性能 粘结性能 

分 类 号:TQ333.93[化学工程—橡胶工业] TQ330.16

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象