原油缓冲罐罐顶的腐蚀与防护对策  

Protection Measures of Corrosion on Top of Crude Oil Buffer Tank

作　　者：赵静[1] 葛金辉 ZHAO Jing;GE Jinhui(SINOPEC Luoyang Company,Luoyang 471012,China)

机构地区：[1]中国石油化工股份有限公司洛阳石化分公司,河南洛阳471012

出　　处：《石油化工腐蚀与防护》2020年第4期25-28,共4页Corrosion & Protection In Petrochemical Industry

摘　　要：罐底穿孔是原油储罐比较常见的腐蚀问题,而罐顶的腐蚀减薄甚至穿孔则一直被忽视,没有引起足够的重视。由于受服役时间长和原油逐年劣质化等因素影响,导致某石化公司零位罐区4台原油缓冲罐罐顶腐蚀减薄严重并有穿孔发生。该文以罐区4台原油缓冲罐罐顶腐蚀减薄穿孔为例,详细分析了罐顶腐蚀的原因,并提出了具体的防护对策。Corrosion perforation at the bottom of crude oil tank is a common problem, but corrosion thinning and perforation at the top of the tank has not attracted widespread attention. Severe corrosion thinning and perforation occurred on the top of four crude oil buffer tanks in a petrochemical company due to the factors such as long service life and deterioration of crude oil quality. Causes of the corrosion were analyzed in detail, and specific protective measures were brought up.

关 键 词：原油缓冲罐 腐蚀机理 防护对策 