Optically stimulated luminescence of Dy^3+-doped NaCaPO4 glass-ceramics  

作　　者：Jie Xu Zhaoyang Chen Minqiang Gai Yanwei Fan Chengfa He 

机构地区：[1]Key Laboratory of Functional Materials and Devices for Special Environments of CAS,Xinjiang Key Laboratory of Electronic Information Materials and Devices,Xinjiang Technical Institute of Physics and Chemistry of CAS,Urumqi 830011,China [2]University of Chinese Academy of Sciences,Beijing 100049,China [3]Laboratory of Solid State Radiation Physics,Urumqi 830011,China

出　　处：《Journal of Rare Earths》2020年第9期927-932,I0001,共7页稀土学报（英文版）

基　　金：Project supported by the National Natural Science Foundation of China(11675260)。

摘　　要：Dy^3+-doped glass-ceramics containing NaCaPO4 crystals were successfully fabricated by heat treatment at base glass,and the luminescence properties were investigated for potential applications in radiation measurements.The photo luminescence(PL)excitation and emission spectra exhibit transitions related to Dy^3+ions corresponding to the strongest excitation and emission wavelengths at 351 and 575 nm,respectively.The CW-OSL properties as a function of dopant concentration,pre-heating temperature,pre-heating time and signal fading were investigated.The most appropriate Dy^3+ion concentration was found to be 0.25 mol%.The TL glow curves have a broad peak feature peaking at 195±5℃.The fading of the OSL signal would keep stable in five days with the intensity value of about 76.11%.The samples also exhibit good signal reusability and a broad linear dose response range(0.02-1000 Gy).

关 键 词：Optically stimulated luminescence GLASS-CERAMICS Radiation measurements PHOTOLUMINESCENCE Rare earths 