高强度耐候钢卷板Q415NHE的生产实践  

Production Practice of High Strength Weathering Coil Sheet of Q415NHE Steel

作　　者：夏志升[1] 王中岐[2] 王新志[2] Xia Zhisheng;Wang Zhongqi;Wang Xinzhi(Anyang Iron and Steel Group Co.,Ltd)

机构地区：[1]安阳钢铁集团有限责任公司技术中心 [2]安阳钢铁集团有限责任公司

出　　处：《特钢技术》2020年第2期21-23,9,共4页Special Steel Technology

摘　　要：本文介绍了高强度耐候钢卷板Q415NHE的生产试验,成分体系上采用低碳成分体系,生产工艺上采用合适的加热和轧制工艺、冷却工艺。生产试验结果表明:当卷取温度为600℃时,Q415NHE组织以F+P为主,晶粒度在10级;屈服强度在450MPa以上,抗拉强度在550MPa以上,伸长率在23%以上;-40℃冲击功在200J以上,整体工艺力学性能良好,完全满足产品技术要求。This paper introduces the production test of Q415NHE high strength weather-resisting coil sheet.The composition system adopts low carbon composition system,and the production process adopts appropriate heating,rolling and cooling processes.The production test results show that:when the coiling temperature is 600℃,the microstructure of Q415NHE is mainly F+P,and the grain size is No.10,the yield strength is more than 450MPa,the tensile strength is above 550MPa,and the elongation is more than 23%,the impact energy at-40℃is above 200J,and the overall process mechanical properties are good,which fully meet the product technical requirements.

关 键 词：生产实践 耐候钢 Q415NHE 

分 类 号：TG142.33[一般工业技术—材料科学与工程]