低Cu高强Al-Zn-Mg-Cu合金搅拌摩擦焊接组织与性能  

Microstructure and Properties of Low Cu and High Strength Al-Zn-Mg-Cu Alloy Friction Stir Welded Joints

作　　者：戴海桃 韦莉莉 黄宏锋 侯远飞 刘帅 Dai Haitao;Wei Lili;Huang Hongfeng;Hou Yuanfei;Liu Shuai(School of Materials Science and Engineering,Guilin University of Technology)

机构地区：[1]桂林理工大学材料科学与工程学院,广西桂林541004

出　　处：《特种铸造及有色合金》2020年第9期934-938,共5页Special Casting & Nonferrous Alloys

基　　金：广西自然科学基金资助项目(2018GXNSFAA138065);有色金属及材料加工新技术教育部重点实验室开放基金资助项目(19KF-3)。

摘　　要：分别采用300、900r/min对低Cu高强Al-Zn-Mg-Cu合金板材进行搅拌摩擦焊接,研究合金焊接接头的显微组织和力学性能。结果表明,焊接过程中微米级AlMnCr相变化不明显,晶内纳米级和晶界亚微米级MgZn2相发生回溶与粗化。随着焊接转速增加,析出相回溶程度加剧,焊接接头晶粒尺寸增大。在晶粒和析出相共同作用下,合金焊接接头硬度呈“U”型分布,前进侧热影响区硬度略低于后退侧,焊核及热机影响区硬度较低,是焊接接头断裂位置,受“S”线缺陷影响形成锯齿形断口形貌。综合分析,低Cu高强Al-Zn-Mg-Cu合金在300r/min下接头性能较好,抗拉强度、屈服强度、伸长率和焊接系数分别为393MPa、261MPa、12%和80%。Friction stir welding of low Cu and high strength Al-Zn-Mg-Cu alloy plate was carried out at 300r/min and 900r/min.The microstructure and mechanical properties of the welded joints were analyzed by means of metallographic microscope,scanning electron microscope,transmission electron microscope,Vickers hardness and tensile test.The results show that there is absence of obvious change of micrometer AlMnCr phase during the welding process,and the dissolution and coarsening occur in intracrystalline nanoscale MgZn2phase and grain boundary submicron MgZn2phase.With the increase of welding speed,the degree of precipitate dissolution is increased,and the grain size of welded joint tends to be increased.Under the combined action of grains and precipitates,the hardness of the welded joints of the alloy is characterized by approximate U-shaped distribution.The hardness of the heat affected zone on the advancing side is slightly lower than that on the retreating side,and that of the welding nugget and heat affected zone is relatively low,which is the fracture position of the welded joints,presenting zigzag fracture shape affected by the"S"line defect.The welded joints of low Cu and high strength Al-Zn-Mg-Cu alloy have the better properties under the low rotational speed of 300r/min.The maximum tensile strength,yield strength,elongation and welding coefficient reach 393MPa,261MPa,12%and 80%,respectively.

关 键 词：AL-ZN-MG-CU合金 搅拌摩擦焊接 焊接转速 力学性能 微观组织 

分 类 号：TG146.21[一般工业技术—材料科学与工程] TG456.7[金属学及工艺—金属材料]